PPO 500V ASAHI JAPAN
XYRON™
Industrial machinery、Automotive Applications
Aging resistance、Chemical resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | ASAHI JAPAN/500V |
|---|---|---|---|
| Shrinkage rate | ASTM D-955 | 0.50-0.70 % | |
| Water absorption rate | ASTM D-570 | 0.10 % | |
| density | ASTM D-792 | 1.08 g/cm |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/500V |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 93 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2350 kg/cm²(MPa)[Lb/in²] | |
| ASTM D-790 | 2400 Mpa | ||
| bending strength | ASTM D-790 | 78 Mpa | |
| tensile strength | ASTM D-638 | 59 Mpa | |
| elongation at break | ASTM D638/ISO 527 | 40 % | |
| Rockwell hardness | ASTM D785 | R116 | |
| elongation at break | ASTM D-638 | 40 % | |
| tensile strength | ASTM D638/ISO 527 | 54 kg/cm²(MPa)[Lb/in²] |
| Physical properties | Test Condition | Test Method | ASAHI JAPAN/500V |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.08 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.1 % |
| processability | Test Condition | Test Method | ASAHI JAPAN/500V |
|---|---|---|---|
| Temperature | 70-100 °C |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/500V |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-1 | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 120 ℃（℉） |
| UL flame retardant rating | UL 94 | V-1 |