POE 8201 EXXONMOBIL HOLLAND
EXACT™
Automotive sector、film、Packaging film
Low temperature resistanc、High temperature resistan、wear resistant、Weather resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | EXXONMOBIL HOLLAND/8201 |
|---|---|---|---|
| Haze ratio | ASTM D1003(A) | 2.2 % | |
| Flexural modulus | 1% secant | ISO 1184(F) | 24/25 Mpa |
| Mooney viscosity ML (1+4) | 125℃ | ASTM D-1646 | 16.5 Torgue Units |
| Maximum resistance to puncture pressure | 内部方法 | 125 Mpa | |
| Impact strength of cantilever beam gap | ASTM D4272 | >18 g/u | |
| Guan Zedu | 45℃ | ASTM 2457 | 84 |
| Breakdown voltage strength | 内部方法 | 1500 MJ/mm |
| Basic performance | Test Condition | Test Method | EXXONMOBIL HOLLAND/8201 |
|---|---|---|---|
| heat of fusion | ASTM D3418 | 105 J/g | |
| Maximum melt temperature | ASTM D3418 | 70 °C | |
| melt mass-flow rate | 2.16kg/190℃ | ISO 1133 | 1.1 dg/min |
| Shore hardness | Shore A | ISO 868 | 85 |
| vicat | at 10 N | ISO 306 | 55 °C |
| density | 23℃ | ISO 1183 | 882 kg/cm |
| Shore hardness | Shore D | ISO 868 | 29 |
| physical property | Test Condition | Test Method | EXXONMOBIL HOLLAND/8201 |
|---|---|---|---|
| Impact strength of cantilever beam gap | @23℃ and @-40℃ | ASTM D256 | No Break J/m |
| tensile strength | 断裂 | ISO 527-2 | 24 Mpa |
| Flexural modulus | ISO 178 | 30 Mpa | |
| Environmental stress cracking resistance | ASTM D-1693 | >1000 hr | |
| elongation at break | ISO 527-2 | 1750 % |