PC 3413R-739 SABIC INNOVATIVE JAPAN
LEXAN™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/3413R-739 |
|---|---|---|---|
| Vicat Softening Temperature | ASTMD15255 | 165 °C | |
| Specific Heat | ASTMC351 | 1130 J/kg/°C | |
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 146 °C |
| RTIElec | UL746 | 120 °C | |
| Thermal Conductivity | ASTMC177 | 0.22 W/m/K | |
| RTIStr | UL746 | 130 °C | |
| Evolution Calendar intelligent importer | UL746 | 120 °C | |
| Linear thermal expansion coefficient | MD：-40到95°C | ASTME831 | 2.2E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTMD648 | 151 °C |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/3413R-739 |
|---|---|---|---|
| Rockwell Hardness | M计秤 | ASTMD785 | 92 |
| R计秤 | ASTMD785 | 120 |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/3413R-739 |
|---|---|---|---|
| Moisture Absorption | 24hr | ASTMD570 | 0.14 % |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.10to0.30 % |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 5.0 g/10min |
| Moisture Absorption | 平衡,23°C | ASTMD570 | 0.26 % |
| Melt Mass-Flow Rate | 300°C/5.0kg | ASTMD1238 | 19 g/10min |
| Specific Volume | ASTMD792 | 0.697 cm³/g |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/3413R-739 |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 6610 Mpa |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 153 Mpa |
| Tensile Elongation | 断裂 | ASTMD638 | 2.0 % |
| Tensile Strength | 断裂 | ASTMD638 | 100 Mpa |
| Taber Abrasion Resistance | 1000Cycles,1000g,CS-17转轮 | ASTMD1044 | 24.0 mg |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/3413R-739 |
|---|---|---|---|
| Gardner Impact | 23°C | ASTMD3029 | 5.00 J |
| Tensile Impact Strength | ASTMD1822 | 67.0 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/3413R-739 |
|---|---|---|---|
| Flame Rating | 0.75mm | UL94 | HB |
| 3.0mm | UL94 | V-0 | |
| 1.5mm | UL94 | V-1 |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/3413R-739 |
|---|---|---|---|
| Dissipation Factor? | 50Hz | ASTMD150 | 1.1E-03 |
| 60Hz | ASTMD150 | 1.1E-03 | |
| 1MHz | ASTMD150 | 7E-03 | |
| Hot-wire Ignition | HWI | UL746 | PLC 0 |
| High Amp Arc Ignition | HAI | UL746 | PLC 4 |
| Volume Resistivity | ASTMD257 | >1.0E+17 ohms·cm | |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC 3 |
| Dielectric Constant | 60Hz | ASTMD150 | 3.35 |
| 50Hz | ASTMD150 | 3.35 | |
| Arc Resistance | ASTMD495 | PLC7 | |
| Dielectric Constant | 1MHz | ASTMD150 | 3.31 |
| Dielectric Strength | 3.20mm,inAir | ASTMD149 | 19 KV/mm |
| Comparative Tracking Index | CTI | UL746 | PLC 5 |