LCP E130i JAPAN POLYPLASTIC
LAPEROS®
Household appliances、Household appliances
heat-resisting、Flame retardant、enhance
UL
SGS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | JAPAN POLYPLASTIC/E130i |
|---|---|---|---|
| Rockwell hardness | M计秤 | ISO 2039-2 | 80 |
| Supplementary Information | Test Condition | Test Method | JAPAN POLYPLASTIC/E130i |
|---|---|---|---|
| ColorNumber | VF2201/BK210P/BK205P |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/E130i |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 220 kg/cm²(MPa)[Lb/in²] | |
| elongation | 断裂 | ASTM D638 | 2.0 % |
| Flexural modulus | ASTM D790/ISO 178 | 15000 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ISO 178 | 220 Mpa | |
| Flexural modulus | ISO 178 | 15000 Mpa | |
| Bending Strain | ISO 178 | 2.3 % | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 35 kg·cm/cm(J/M)ft·lb/in | |
| tensile strength | ASTM D638/ISO 527 | 175 kg/cm²(MPa)[Lb/in²] | |
| ASTM D638 | 175 Mpa |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/E130i |
|---|---|---|---|
| Dissipation Factor | 1kHz | IEC 60250 | 0.020 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 4 | |
| relative permittivity | 1kHz | IEC 60250 | 4.30 |
| dielectric strength | 1.00mm | IEC 60243-1 | 44 KV/mm |
| Dissipation Factor | 耐电弧性 | IEC 60250 | 130 sec |
| Volume resistivity | IEC 60093 | 9E+15 ohms·cm | |
| dielectric strength | 3.00mm | IEC 60243-1 | 24 KV/mm |
| relative permittivity | 1MHz | IEC 60250 | 3.80 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.030 |
| other | Test Condition | Test Method | JAPAN POLYPLASTIC/E130i |
|---|---|---|---|
| characteristic | 高耐热. 高流动.玻璃纤维. 标准 | ||
| Color | VF2201/BK210P/BK205P/BK211P |
| Physical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/E130i |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.61 |
| flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/E130i |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/E130i |
|---|---|---|---|
| Shrinkage rate | TD:1.00mm | 内部方法 | 0.54 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.030 % |
| Shrinkage rate | MD:1.00mm | 内部方法 | 0.020 % |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/E130i |
|---|---|---|---|
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 280 ℃（℉） |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 290 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 280 °C |