Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO 731S-780S SABIC INNOVATIVE SHANGHAI
NORYL™
Food containers
High mobility、Antistatic、High temperature resistan、currency
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/731S-780S |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 30 % |
| bending strength | 屈服, 50.0 mm 跨距 | ASTM D790 | 93.0 Mpa |
| tensile strength | 屈服 | ASTM D638 | 58.0 Mpa |
| Flexural modulus | 50.0 mm 跨距 | ASTM D790 | 2420 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/731S-780S |
|---|---|---|---|
| Dissipation Factor | 60 Hz | ASTM D150 | 2.7 |
| 50 Hz | ASTM D150 | 2.7 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/731S-780S |
|---|---|---|---|
| Water absorption rate | 24 hr | ASTM D570 | 0.060 % |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.50 - 0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/731S-780S |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 126 °C |
| RTI Imp | UL 746 | 90.0 °C | |
| RTI | UL 746 | 105 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 117 °C |
| Linear coefficient of thermal expansion | -40 到 60°C，流动 | ASTM E831 | 1.3E-4 cm/cm/°C |
| RTI Elec | UL 746 | 105 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/731S-780S |
|---|---|---|---|
| drying time | 2.0 to 4.0 hr | ||
| Processing (melt) temperature | 280 to 310 °C | ||
| drying temperature | 105 to 110 °C | ||
| Temperature | 70 to 95 °C |