PC Kingfa JH960 6300 Kingfa
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Kingfa/Kingfa JH960 6300 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 470 J/m |
| -10°C,3.20mm | ASTM D256 | 380 J/m |
| hardness | Test Condition | Test Method | Kingfa/Kingfa JH960 6300 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 118 |
| Mechanical properties | Test Condition | Test Method | Kingfa/Kingfa JH960 6300 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 50 % |
| tensile strength | ASTM D638 | 55.0 MPa | |
| Flexural modulus | ASTM D790 | 2600 MPa | |
| bending strength | ASTM D790 | 85.0 MPa |
| Electrical performance | Test Condition | Test Method | Kingfa/Kingfa JH960 6300 |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 1E+15 ohms | |
| dielectric strength | 1.60mm | ASTM D149 | 19 kV/mm |
| flammability | Test Condition | Test Method | Kingfa/Kingfa JH960 6300 |
|---|---|---|---|
| UL flame retardant rating | 3.20mm | UL 94 | V-0 |
| 1.60mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | Kingfa/Kingfa JH960 6300 |
|---|---|---|---|
| melt mass-flow rate | 260°C/2.16kg | ASTM D1238 | 19 g/10min |
| Shrinkage rate | MD：23°C | ASTM D955 | 0.50to0.70 % |
| density | ASTM D792 | 1.19 g/cm³ |
| Thermal performance | Test Condition | Test Method | Kingfa/Kingfa JH960 6300 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 88.0 °C |
| 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 100 °C |