Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ASA XTPMFR10-WH9F029 SABIC INNOVATIVE NANSHA
GELOY™
Automotive Applications、Electrical applications
Thermal stability、Antistatic、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/XTPMFR10-WH9F029 |
|---|---|---|---|
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 85.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/XTPMFR10-WH9F029 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 66.0 Mpa |
| Bending modulus 5 | ISO 178 | 2720 Mpa | |
| elongation | 断裂 | ISO 527-2/50 | 21 % |
| tensile strength | 断裂 | ISO 527-2/5 | 46.0 Mpa |
| elongation | 屈服 3 | ASTM D638 | 4.0 % |
| Tensile modulus | -- 2 | ASTM D638 | 2680 Mpa |
| tensile strength | 屈服 3 | ASTM D638 | 65.0 Mpa |
| elongation | 屈服 4 | ASTM D638 | 4.0 % |
| tensile strength | 屈服 4 | ASTM D638 | 60.0 Mpa |
| Bending stress 5, 6 | ISO 178 | 97.0 Mpa | |
| tensile strength | 断裂 | ISO 527-2/50 | 47.0 Mpa |
| 断裂 4 | ASTM D638 | 49.0 Mpa | |
| 屈服 | ISO 527-2/5 | 61.0 Mpa | |
| Tensile modulus | -- | ISO 527-2/1 | 2680 Mpa |
| elongation | 断裂 3 | ASTM D638 | 31 % |
| tensile strength | 断裂 3 | ASTM D638 | 47.0 Mpa |
| elongation | 断裂 | ISO 527-2/5 | 50 % |
| 屈服 | ISO 527-2/5, ISO 527-2/50 | 4.0 % | |
| 断裂 4 | ASTM D638 | 58 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/XTPMFR10-WH9F029 |
|---|---|---|---|
| UL flame retardant rating | 1.0 mm, Testing by SABIC | UL 94 | V-0 |
| Filling analysis | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/XTPMFR10-WH9F029 |
|---|---|---|---|
| melt viscosity | 260°C, 1500 sec^-1 | ISO 11443 | 105 Pa·s |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/XTPMFR10-WH9F029 |
|---|---|---|---|
| Molten Volume Flow Rate (MVR) | 260°C/2.16 kg | ISO 1133 | 30.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/XTPMFR10-WH9F029 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 98.0 °C |
| Hot deformation temperature 8 | 0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 | ISO 75-2/Bf | 90.0 °C |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 | ISO 75-2/Af | 81.0 °C | |
| vicat | -- | ISO 306/B50 | 96.0 °C |
| 流动 : -40 到 40°C | ISO 11359-2 | 6.3E-5 cm/cm/°C | |
| 横向 : -40°C | ISO 11359-2 | 6.3E-5 cm/cm/°C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/XTPMFR10-WH9F029 |
|---|---|---|---|
| Temperature | 50 到 70 °C | ||
| Temperature at the rear of the barrel | 200 到 230 °C | ||
| Processing (melt) temperature | 230 到 270 °C | ||
| drying temperature | 80 到 90 °C | ||
| Temperature at the front of the material cylinder | 230 到 270 °C | ||
| drying time | 2.0 到 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Spray nozzle temperature | 220 到 260 °C | ||
| Hopper temperature | 60 到 80 °C | ||
| Temperature in the middle of the barrel | 220 到 260 °C |