PC D251-701 SABIC INNOVATIVE NANSHA
LNP™ THERMOCOMP™ 
Electronic and Electrical、Plastic bag
Non chloro non bromine fl、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/D251-701
Charpy Notched Impact Strength23°CISO 179/1eA14 kJ/m²
Suspended wall beam without notch impact strength23°CASTM D4812720 J/m
Impact strength of simply supported beam without notch23°CISO 179/1eU51 kJ/m²
Dart impact23°C,EnergyatPeakLoadASTM D376322.0 J
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/D251-701
dielectric constant1.90GHz内部方法3.20
Dissipation Factor5.00GHz内部方法6.4E-03
dielectric constant20.0GHz内部方法3.20
Dissipation Factor1.90GHz内部方法6.3E-03
10.0GHz内部方法6.7E-03
dielectric constant1.10GHz内部方法3.20
Dissipation Factor1.10GHz内部方法6.3E-03
dielectric constant10.0GHz内部方法3.20
Dissipation Factor20.0GHz内部方法6.5E-03
dielectric constant5.00GHz内部方法3.20
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/D251-701
fractureISO 527-2/5112 Mpa
ASTM D6382.7 %
--6ISO 178165 Mpa
--5ISO 1786240 Mpa
fractureASTM D638110 Mpa
50.0mm spanASTM D7906150 Mpa
--1ASTM D6386680 Mpa
fractureISO 527-2/52.6 %
Fracture, 50.0mm spanASTM D790167 Mpa
flammabilityTest ConditionTest MethodSABIC INNOVATIVE NANSHA/D251-701
UL flame retardant rating0.600mmUL 94V-0
0.500mmUL 94V-1
0.300mmUL 94V-2
physical property Test ConditionTest MethodSABIC INNOVATIVE NANSHA/D251-701
melt mass-flow rate300°C/2.16kgASTM D123833 g/10min
Shrinkage rateTD:24小时ASTM D9550.20-0.40 %
Melt volume flow rate300°C/1.2kgISO 113315.0 cm3/10min
Water absorption rate平衡,23°C,50%RHISO 620.030 %
饱和,23°CISO 620.070 %
densityASTM D7921.35 g/cm³
Shrinkage rateMD:24小时ASTM D9550.20-0.40 %
Melt volume flow rate300°C/2.16kgISO 113329.0 cm3/10min
melt mass-flow rate300°C/1.2kgASTM D123817 g/10min
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/D251-701
Linear coefficient of thermal expansionTD:23到80°CISO 11359-27.3E-05 cm/cm/°C
Heat distortion temperature0.45MPa,未退火,3.20mm，HDTASTM D648121 °C
Linear coefficient of thermal expansionMD:23到80°CISO 11359-22.6E-05 cm/cm/°C
Heat distortion temperature1.8MPa,未退火,3.20mm，HDTASTM D648116 °C