ABS J-1200/CF/10 USA TLC
--
Automotive electronics, bushings, enterprise equipment, conveyor parts, packaging
Anti static and conductive
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Basic performance | Test Condition | Test Method | USA TLC/J-1200/CF/10 |
---|---|---|---|
Water absorption rate | 24hr | ASTM D-570 | 0.40 % |
Mechanical properties | Test Condition | Test Method | USA TLC/J-1200/CF/10 |
---|---|---|---|
tensile strength | 23℃,断裂 | ASTM D-638 | 82.7 MPa |
Impact strength of cantilever beam gap | 23℃,3.18mm | ASTM D-256 | 42.7 J/m |
elongation at break | 23℃ | ASTM D-638 | 1.7 % |
bending strength | 23℃,断裂 | ASTM D-790 | 110 MPa |
Tensile modulus | 23℃ | ASTM D-638 | 7580 MPa |
Suspended wall beam without notch impact strength | 23℃,3.18mm | ASTM D-256 | 187 J/m |
Flexural modulus | 23℃ | ASTM D-790 | 6890 MPa |
Electrical performance | Test Condition | Test Method | USA TLC/J-1200/CF/10 |
---|---|---|---|
Surface Resistivity | ASTM D-257 | 5E+02 ohms | |
Volume resistivity | ASTM D-257 | 50 ohm.cm |
physical property | Test Condition | Test Method | USA TLC/J-1200/CF/10 |
---|---|---|---|
density | ASTM D-792 | 1.10 g/cm | |
Shrinkage rate | Flow | ASTM D-955 | 0.10 % |
Thermal performance | Test Condition | Test Method | USA TLC/J-1200/CF/10 |
---|---|---|---|
combustibility | 1.59mm | UL 94 | HB |
Heat distortion temperature | 0.45MPa,未退火,HDT | ASTM D-648 | 104 ℃ |
1.80MPa,未退火,HDT | ASTM D-648 | 98.9 ℃ |