Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PCTA Z6006 EASTMAN USA
Eastar™
Higher impact strength、Can replace transparent A
transparent、Crystallization occurs at、Balanced mold temperature、No hot spots
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | EASTMAN USA/Z6006 |
|---|---|---|---|
| intrinsic viscosity | 0.72 |
| Basic performance | Test Condition | Test Method | EASTMAN USA/Z6006 |
|---|---|---|---|
| melt mass-flow rate | 230℃,5kg | 15 g/10min |
| Mechanical properties | Test Condition | Test Method | EASTMAN USA/Z6006 |
|---|---|---|---|
| Tensile stress | 屈服 | ASTM D-638 | 6700/7700 psi |
| Rockwell hardness | ASTM D-785 | 105 R | |
| tensile strength | 屈服 | ASTM D-790 | 9700 psi |
| Impact strength of cantilever beam gap | 23℃/-40℃ | ASTM D-256 | 7/1.1 ft-lb/in |
| Flexural modulus | ASTM D-790 | 2.75×105 psi | |
| elongation at break | ASTM D-638 | 5/310 % |
| physical property | Test Condition | Test Method | EASTMAN USA/Z6006 |
|---|---|---|---|
| transmittance | ASTM D-1003 | 91 % | |
| Shrinkage rate | 3.2mm(0.125in) | ASTM D-955 | 0.002-0.006 in/in |
| Haze ratio | ASTM D-1003 | 0.3 % |
| Thermal performance | Test Condition | Test Method | EASTMAN USA/Z6006 |
|---|---|---|---|
| combustibility | 3.0mm | UL 94 | V-2 |
| vicat | 1kg负荷 | ASTM D-1525 | 85 °C |
| Heat distortion temperature | 1.82MPa(264PSi)，HDT | ASTM D-648 | 65 °C |
| 0.45MPa(66PSi)，HDT | ASTM D-648 | 73 °C |