Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PBT X5300WX-RO2453 SABIC INNOVATIVE US
XENOY™
Electronic and electrical
Chemical resistance、Weather resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/X5300WX-RO2453 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 45 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 71.0 J |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 15 kJ/m² |
| 23°C | ISO 180/1A | 50 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/X5300WX-RO2453 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2250 Mpa | |
| elongation | 屈服 | ASTM D638 | 5.0 % |
| tensile strength | 断裂 | ASTM D638 | 51.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 5.0 % |
| tensile strength | 断裂 | ISO 527-2/50 | 51.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2480 Mpa |
| Tensile modulus | ASTM D638 | 2550 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 62.0 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 96.0 Mpa |
| elongation | 断裂 | ASTM D638 | 110 % |
| bending strength | ISO 178 | 87.0 Mpa | |
| Flexural modulus | ISO 178 | 2180 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 62.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 110 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/X5300WX-RO2453 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.70-0.90 % |
| melt mass-flow rate | 266°C/5.0kg | ASTM D1238 | 26 g/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.15 % |
| 饱和,23°C | ISO 62 | 0.50 % | |
| Melt volume flow rate | 265°C/5.0kg | ISO 1133 | 25.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/X5300WX-RO2453 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 124 °C |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 88.0 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 7.6E-05 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 7.5E-05 cm/cm/°C | |
| vicat | -- | ISO 306/B50 | 120 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 101 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ISO 11359-2 | 7E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 89.0 °C |
| vicat | ASTM D152510 | 135 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 87.0 °C |