Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT/PET 8032UX BK1A404U SABIC INNOVATIVE US
VALOX™
chip、Shell、Home appliance components、Phone case
enhance、Filler: Glass fiber reinf、30%、Filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/8032UX BK1A404U |
|---|---|---|---|
| 23°C | ASTMD4812 | 480 J/m | |
| The impact strength of a simply supported beam without a notch is 13 | -30°C | ISO179/1eU | 40 kJ/m² |
| Impact strength of simply supported beam gap 12 | -30°C | ISO179/1eA | 9.0 kJ/m² |
| -30°C | ASTMD256 | 48 J/m | |
| 0°C15 | ISO180/1A | 8.0 kJ/m² | |
| Impact strength of simply supported beam gap 12 | 23°C | ISO179/1eA | 9.0 kJ/m² |
| -30°C17 | ISO180/1U | 40 kJ/m² | |
| 23°C | ASTMD256 | 57 J/m | |
| The impact strength of a simply supported beam without a notch is 13 | 23°C | ISO179/1eU | 45 kJ/m² |
| -30°C14 | ISO180/1A | 8.0 kJ/m² | |
| -30°C | ASTMD4812 | 470 J/m | |
| 23°C18 | ISO180/1U | 45 kJ/m² | |
| 23°C16 | ISO180/1A | 9.0 kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 8.00 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/8032UX BK1A404U |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO2039-2 | 119 |
| H358/30 | ISO2039-1 | 110 Mpa |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/8032UX BK1A404U |
|---|---|---|---|
| yield | ISO527-2/5 | 145 Mpa | |
| --10 | ISO178 | 210 Mpa | |
| fracture | ISO527-2/5 | 2.5 % | |
| 50.0mm span 8 | ASTMD790 | 8450 Mpa | |
| Fracture 5 | ASTMD638 | 115 Mpa | |
| Fracture 7 | ASTMD638 | 2.0 % | |
| --9 | ISO178 | 8500 Mpa | |
| Yield, 50.0mm span 11 | ASTMD790 | 165 Mpa | |
| --3 | ASTMD638 | 9950 Mpa | |
| 1000Cycles,1000g,CS-17转轮 | 内部方法 | 30.0 mg | |
| yield | ISO527-2/5 | 2.4 % | |
| Surrender 6 | ASTMD638 | 2.0 % | |
| fracture | ISO527-2/5 | 145 Mpa | |
| Surrender 4 | ASTMD638 | 115 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/8032UX BK1A404U |
|---|---|---|---|
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| 50Hz | IEC60250 | 3.30 | |
| Dissipation Factor | 60Hz | IEC60250 | 8E-04 |
| dielectric strength | 1.60mm,在油中 | IEC60243-1 | 23 KV/mm |
| Dissipation Factor | 50Hz | IEC60250 | 8E-04 |
| 1MHz | IEC60250 | 0.013 | |
| dielectric strength | 0.800mm,在油中 | IEC60243-1 | 27 KV/mm |
| 1MHz | IEC60250 | 3.20 | |
| 60Hz | IEC60250 | 3.30 | |
| 100Hz | IEC60250 | 3.60 | |
| CTI | IEC60112 | 300 V | |
| dielectric strength | 3.20mm,在油中 | IEC60243-1 | 15 KV/mm |
| Volume resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL746 | PLC 2 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/8032UX BK1A404U |
|---|---|---|---|
| UL flame retardant rating | 1.60mm,TestingbySABIC | UL94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/8032UX BK1A404U |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.050 % |
| Shrinkage rate | TD2 | 内部方法 | 0.60到1.0 % |
| Water absorption rate | 饱和,23°C | ISO62 | 0.16 % |
| Melt volume flow rate | 265°C/2.16kg | ISO1133 | 15.0 cm3/10min |
| Shrinkage rate | MD:3.20mm | 内部方法 | 0.40到0.80 % |
| melt mass-flow rate | 265°C/2.16kg | ASTMD1238 | 15 g/10min |
| Shrinkage rate | TD:3.20mm | 内部方法 | 0.60到1.0 % |
| MD1 | 内部方法 | 0.40到0.80 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/8032UX BK1A404U |
|---|---|---|---|
| 0.45MPa, Unanealed, 100mm span 19 | ISO75-2/Be | 217 °C | |
| 1.8MPa, Unanealed, 100mm span 20 | ISO75-2/Ae | 195 °C | |
| BallPressure Test | 125°C | IEC60695-10-2 | Pass |
| Flow: -40 to 40 ° C | ASTME831 | 2.5E-05 cm/cm/°C | |
| Horizontal: -40 to 40 ° C | ASTME831 | 7.5E-05 cm/cm/°C | |
| 0.45MPa, Unanealed, 3.20mm | ASTMD648 | 208 °C | |
| Horizontal: 23 to 60 ° C | ISO11359-2 | 8.1E-05 cm/cm/°C | |
| Flow: 23 to 60 ° C | ISO11359-2 | 2.2E-05 cm/cm/°C | |
| 1.8MPa, Unanealed, 3.20mm | ASTMD648 | 190 °C |