Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS MG47F-NA1000 SABIC INNOVATIVE MEXICO
CYCOLAC™
--
High impact resistance
UL
FDA
RoHS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE MEXICO/MG47F-NA1000 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 26 kJ/m² |
| -30°C | ISO 179/1eA | 9.0 kJ/m² | |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 30.0 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE MEXICO/MG47F-NA1000 |
|---|---|---|---|
| Rockwell hardness | R 级 | ASTM D785 | 112 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE MEXICO/MG47F-NA1000 |
|---|---|---|---|
| Tensile modulus | --1 | ASTM D638 | 2270 Mpa |
| tensile strength | 屈服2 | ASTM D638 | 44.0 Mpa |
| elongation | 断裂2 | ASTM D638 | 24 % |
| 断裂 | ISO 527-2/50 | 25 % | |
| Flexural modulus | --4 | ISO 178 | 2200 Mpa |
| bending strength | 屈服, 50.0 mm 跨距3 | ASTM D790 | 70.0 Mpa |
| --4,5 | ISO 178 | 70.0 Mpa | |
| Flexural modulus | 50.0 mm 跨距3 | ASTM D790 | 2300 Mpa |
| tensile strength | 断裂 | ISO 527-2/50 | 35.0 Mpa |
| 屈服 | ISO 527-2/50 | 47.0 Mpa | |
| elongation | 屈服2 | ASTM D638 | 2.0 % |
| 屈服 | ISO 527-2/50 | 2.6 % | |
| tensile strength | 断裂2 | ASTM D638 | 33.0 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 2370 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE MEXICO/MG47F-NA1000 |
|---|---|---|---|
| Hot wire ignition (HWI) | UL 746 | PLC 3 | |
| arc resistance | ASTM D495 | PLC 6 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 3 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 0 | |
| High arc combustion index (HAI) | UL 746 | PLC 0 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE MEXICO/MG47F-NA1000 |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| Filling analysis | Test Condition | Test Method | SABIC INNOVATIVE MEXICO/MG47F-NA1000 |
|---|---|---|---|
| melt viscosity | 240°C, 1000 sec^-1 | ASTM D3835 | 225 Pa·s |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE MEXICO/MG47F-NA1000 |
|---|---|---|---|
| melt mass-flow rate | 230°C/3.8 kg | ASTM D1238 | 5.6 g/10 min |
| 220°C/10.0 kg | ISO 1133 | 18 g/10 min | |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.50 - 0.80 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE MEXICO/MG47F-NA1000 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 8.8E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距7，HDT | ISO 75-2/Af | 81.0 °C |
| vicat | -- | ISO 306/B120 | 100 °C |
| -- | ASTM D15258 | 99.0 °C | |
| -- | ISO 306/B50 | 98.0 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 94.0 °C |
| RTI Imp | UL 746 | 60.0 °C | |
| Linear coefficient of thermal expansion | 横向 : -40 到 40°C | ASTM E831 | 8.8E-5 cm/cm/°C |
| RTI | UL 746 | 60.0 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 80.0 °C |
| RTI Elec | UL 746 | 60.0 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE MEXICO/MG47F-NA1000 |
|---|---|---|---|
| screw speed | 30 to 60 rpm | ||
| Suggested maximum moisture content | 0.10 % | ||
| Processing (melt) temperature | 220 to 260 °C | ||
| drying temperature | 80 to 95 °C | ||
| Suggested injection volume | 50 to 70 % | ||
| drying time | 2.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 205 to 225 °C | ||
| Temperature at the rear of the barrel | 190 to 210 °C | ||
| Exhaust hole depth | 0.038 to 0.051 mm | ||
| Temperature at the front of the material cylinder | 215 to 240 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 50 to 70 °C | ||
| Spray nozzle temperature | 220 to 260 °C |