Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 201-10 Trinseo
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Trinseo/201-10 |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eU2 | NoBreak |
| 23°C | ISO 179/1eU2 | NoBreak | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/4A | 88 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA2 | 13.0 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | NoBreak |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA2 | 90.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Trinseo/201-10 |
|---|---|---|---|
| Tensile modulus | ISO 527-22 | 2300 MPa | |
| Tensile strain | 屈服 | ISO 527-22 | 6.0 % |
| Nominal fracture strain | ISO 527-22 | >50 % | |
| tensile strength | 屈服 | ISO 527-22 | 60.0 MPa |
| Tensile modulus | ISO 527-2/50 | 2300 MPa | |
| Flexural modulus | ISO 178 | 2400 MPa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 150 % |
| 屈服 | ISO 527-2/50 | 6.0 % | |
| tensile strength | 屈服 | ISO 527-2/50 | 60.0 MPa |
| bending strength | ISO 178 | 97.0 MPa | |
| tensile strength | 断裂 | ISO 527-2/50 | 71.0 MPa |
| Electrical performance | Test Condition | Test Method | Trinseo/201-10 |
|---|---|---|---|
| Volume resistivity | IEC 600932 | >1.0E+13 ohms·m | |
| relative permittivity | 1MHz | IEC 602502 | 3.00 |
| Dissipation Factor | 1MHz | IEC 602502 | 2E-03 |
| 100Hz | IEC 602502 | 1E-03 | |
| Compared to the Leakage Tracking Index (CTI) | 2.00mm | IEC 60112 | PLC 2 |
| dielectric strength | IEC 60243-12 | 17 kV/mm | |
| relative permittivity | 100Hz | IEC 602502 | 3.00 |
| optical performance | Test Condition | Test Method | Trinseo/201-10 |
|---|---|---|---|
| transmissivity | ASTM D1003 | 87.0to91.0 % |
| flammability | Test Condition | Test Method | Trinseo/201-10 |
|---|---|---|---|
| Burning Behav.atthicknessh | 3.20mm,UL | ISO 12102 | HB |
| Limiting Oxygen Index (LOI) | ISO 4589-22 | 26 % | |
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| Burning Behav. | 1.60mm,UL | ISO 12102 | HB |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Trinseo/201-10 |
|---|---|---|---|
| Melt volume flow rate | 300°C/1.2kg | ISO 11332 | 8.00 cm³/10min |
| Shrinkage rate | MD | ISO 294-4 | 0.50to0.70 % |
| density | ISO 1183/A | 1.20 g/cm³ | |
| ISO 11832 | 1200 kg/m³ | ||
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 10 g/10min |
| Thermal performance | Test Condition | Test Method | Trinseo/201-10 |
|---|---|---|---|
| vicat | 50N | ISO 3062 | 149 °C |
| Ball pressure temperature | IEC 60335-1 | 125 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-22 | 7E-05 cm/cm/°C |
| vicat | ISO 306/B50 | 149 °C | |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 141 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 125 °C | |
| 1.8MPa，HDT | ISO 75-22 | 131 °C | |
| 0.45MPa，HDT | ISO 75-22 | 145 °C | |
| 0.45MPa,退火，HDT | ISO 75-2/B | 144 °C |