Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS GR-2000 DENKA JAPAN
DENKA
Electronic field、Electrical field
High temperature resistan、Flame retardant、transparent、High impact resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | DENKA JAPAN/GR-2000 |
|---|---|---|---|
| Surface intrinsic resistance | JIS K8911 | >1010 Ω |
| Basic performance | Test Condition | Test Method | DENKA JAPAN/GR-2000 |
|---|---|---|---|
| melt mass-flow rate | 23℃ | ASTM D-1238 | 12 g/10min |
| Mechanical properties | Test Condition | Test Method | DENKA JAPAN/GR-2000 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 70 kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 225 kg·cm/cm(J/M)ft·lb/in | |
| Shore hardness | 23℃ | ASTM D-785 | 117 |
| Flexural modulus | ASTM D790/ISO 178 | 2.4 kg/cm²(MPa)[Lb/in²] | |
| 15mm/min | ASTM D-790 | 2500 Mpa | |
| Impact strength of cantilever beam gap | 23℃ | ASTM D-256 | 225 J/m |
| tensile strength | 5mm/min | ASTM D-638 | 47 Mpa |
| bending strength | 15mm/min | ASTM D-790 | 75 Mpa |
| other | Test Condition | Test Method | DENKA JAPAN/GR-2000 |
|---|---|---|---|
| characteristic | 标准级 | ||
| purpose | 高冲击 |
| Physical properties | Test Condition | Test Method | DENKA JAPAN/GR-2000 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.4-0.6 % | |
| density | ASTM D792/ISO 1183 | 1.04 |
| physical property | Test Condition | Test Method | DENKA JAPAN/GR-2000 |
|---|---|---|---|
| Shrinkage rate | 2mmt | 0.4-0.6 % |
| Thermal performance | Test Condition | Test Method | DENKA JAPAN/GR-2000 |
|---|---|---|---|
| Heat distortion temperature | 18.6kg，HDT | ASTM D-648 | 90 °C |
| HDT | ASTM D648/ISO 75 | 89 ℃（℉） | |
| combustibility | UL 94 | HB | |
| vicat | 5kg | ASTM D-1525 | 102 °C |