PA66 Generic Nylon 66/6 - Glass Fiber Generic
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Generic/Generic Nylon 66/6 - Glass Fiber |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 4.9to15 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | 39to51 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 43to160 J/m |
| 23°C | ISO 180 | 2.9to16 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 29to95 kJ/m² |
| hardness | Test Condition | Test Method | Generic/Generic Nylon 66/6 - Glass Fiber |
|---|---|---|---|
| Shore hardness | 23°C | ISO 868 | 84to85 |
| ball-indentation hardness | ISO 2039-1 | 160to274 MPa |
| Mechanical properties | Test Condition | Test Method | Generic/Generic Nylon 66/6 - Glass Fiber |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 5440to9110 MPa |
| bending strength | 23°C | ASTM D790 | 130to291 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 1.9to4.0 % |
| 断裂,23°C | ASTM D638 | 3.0to5.1 % | |
| Tensile modulus | 23°C | ISO 527-2 | 5200to16800 MPa |
| tensile strength | 屈服,23°C | ISO 527-2 | 80.0to250 MPa |
| 23°C | ASTM D638 | 143to174 MPa | |
| Tensile strain | 屈服,23°C | ISO 527-2 | 2.0to3.0 % |
| tensile strength | 断裂,23°C | ISO 527-2 | 110to242 MPa |
| Flexural modulus | 23°C | ASTM D790 | 4230to9520 MPa |
| bending strength | 23°C | ISO 178 | 144to286 MPa |
| Electrical performance | Test Condition | Test Method | Generic/Generic Nylon 66/6 - Glass Fiber |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| relative permittivity | 23°C | IEC 60250 | 3.56 |
| dielectric strength | 23°C | IEC 60243-1 | 21to35 kV/mm |
| Volume resistivity | 23°C | IEC 60093 | 1.0E+12到2.5E+15 ohms·cm |
| Surface Resistivity | IEC 60093 | 1.0E+11到2.5E+14 ohms |
| flammability | Test Condition | Test Method | Generic/Generic Nylon 66/6 - Glass Fiber |
|---|---|---|---|
| Hot filament ignition temperature | IEC 60695-2-13 | 650to960 °C | |
| Burning wire flammability index | IEC 60695-2-12 | 650to960 °C | |
| Limiting Oxygen Index | ISO 4589-2 | 21to27 % |
| physical property | Test Condition | Test Method | Generic/Generic Nylon 66/6 - Glass Fiber |
|---|---|---|---|
| Shrinkage rate | 23°C | ISO 294-4 | 0.10to0.91 % |
| MD:23°C | ASTM D955 | 0.20to0.65 % | |
| density | 23°C | ISO 1183 | 1.20to1.58 g/cm³ |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.63to5.8 % |
| 平衡,23°C,50%RH | ISO 62 | 1.5to2.0 % | |
| 23°C,24hr | ASTM D570 | 0.35to1.8 % | |
| 饱和,23°C | ISO 62 | 5.0to8.0 % | |
| density | -- | ASTM D792 | 1.23to1.70 g/cm³ |
| Thermal performance | Test Condition | Test Method | Generic/Generic Nylon 66/6 - Glass Fiber |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 210to250 °C |
| vicat | ISO 306 | 195to241 °C | |
| melting temperature | -- | ISO 11357-3 | 260 °C |
| -- | ISO 3146 | 242to262 °C | |
| RTI | UL 746 | 65.0to67.1 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 224to256 °C |
| Continuous use temperature | ASTM D794 | 100to230 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 199to253 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.5E-5到3.0E-5 cm/cm/°C |
| RTI Imp | UL 746 | 65.0to66.1 °C | |
| Heat distortion temperature | 8.0MPa,未退火，HDT | ISO 75-2/C | 60.0to176 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 7.0E-5到1.1E-4 cm/cm/°C |
| RTI Elec | UL 746 | 65.0to67.1 °C |