Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA46 TE250F6 BL65300 DSM HOLAND
Stanyl®
Automotive Applications、Home appliance components
High temperature resistan、Chemical resistance、enhance、wear resistant、Thermal stability、High rigidity、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DSM HOLAND/TE250F6 BL65300 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 13 kJ/m² |
| -30°C | ISO 179/1eA | 13 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 65 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 13 kJ/m² |
| -40°C | ISO 180/1A | 13 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 50 kJ/m² |
| Mechanical properties | Test Condition | Test Method | DSM HOLAND/TE250F6 BL65300 |
|---|---|---|---|
| tensile strength | 断裂, 160°C | ISO 527-2 | 120 Mpa |
| Flexural modulus | 160°C | ISO 178 | 9000 Mpa |
| Tensile modulus | -- | ISO 527-2 | 17000 Mpa |
| Tensile strain | 断裂, 120°C | ISO 527-2 | 3.0 % |
| 断裂 | ISO 527-2 | 2.0 % | |
| 断裂, 160°C | ISO 527-2 | 3.0 % | |
| Flexural modulus | 120°C | ISO 178 | 10500 Mpa |
| tensile strength | 断裂 | ISO 527-2 | 200 Mpa |
| Flexural modulus | -- | ISO 178 | 15000 Mpa |
| tensile strength | 断裂, 120°C | ISO 527-2 | 130 Mpa |
| Tensile modulus | 160°C | ISO 527-2 | 10000 Mpa |
| 120°C | ISO 527-2 | 11000 Mpa |
| Electrical performance | Test Condition | Test Method | DSM HOLAND/TE250F6 BL65300 |
|---|---|---|---|
| relative permittivity | 100 Hz | IEC 60250 | 4.30 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
| dielectric strength | IEC 60243-1 | 30 KV/mm | |
| Volume resistivity | IEC 60093 | 1.0E+15 ohms·cm | |
| relative permittivity | 1 MHz | IEC 60250 | 4.00 |
| flammability | Test Condition | Test Method | DSM HOLAND/TE250F6 BL65300 |
|---|---|---|---|
| Flammability level | UL 94 | V-0 |
| physical property | Test Condition | Test Method | DSM HOLAND/TE250F6 BL65300 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 1.3 % |
| density | ISO 1183 | 1.82 g/cm³ | |
| Shrinkage rate | 流量 | ISO 294-4 | 0.30 % |
| 横向流量 | ISO 294-4 | 0.90 % |
| Thermal performance | Test Condition | Test Method | DSM HOLAND/TE250F6 BL65300 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 295 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 290 °C |
| RTI Elec | 0.75 mm | UL 746 | 140 °C |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 290 °C |
| Thermal Index - 5000 hr | IEC 60216 | 163 °C | |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 2.0E-5 cm/cm/°C |
| 横向 | ISO 11359-2 | 4.5E-5 cm/cm/°C |