Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 CM3006 TORAY JAPAN
Amilan® 
Automotive sector、Electrical components
Thermal stability、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodTORAY JAPAN/CM3006
Impact strength of simply supported beam without notch23°C无断裂 --
-40°C无断裂 --
hardnessTest ConditionTest MethodTORAY JAPAN/CM3006
Rockwell hardnessR计秤,23°C119
R计秤,80°C97 --
Basic performanceTest ConditionTest MethodTORAY JAPAN/CM3006
Water absorption rate23℃，24小时ASTM D-5703.5%水｜- %
Mechanical propertiesTest ConditionTest MethodTORAY JAPAN/CM3006
Taber abraser1000Cyclesmg8.00 --
Impact strength of cantilever beam gap23℃，V缺口1/2ASTM D-2563.5%水｜28 kg·cm/cm
tensile strength 23°CMPa80.0 50.0
23℃，屈服ASTM D-638无水｜800 kg/cm2
bending strength23℃ASTM D-7903.5%水｜650 kg/cm2
Flexural modulus-40°CMPa4300 4100
bending strengthASTM D790/ISO 1782.8 kg·cm/cm(J/M)ft·lb/in
Flexural modulus80℃ASTM D-7903.5%水｜5000 kg/cm2
Rockwell hardness23℃ASTM D-7853.5%水｜100 R-标度
compressive strength23℃ASTM D-6953.5%水｜- kg/cm2
Rockwell hardness23℃ASTM D-7853.5%水｜- M-标度
bending strength23°CMPa115 65.0
tensile strength 80°CMPa40.0 40.0
Tensile strain断裂,23°C%25
bending strength80°CMPa65.0 40.0
shear strength23°CMPa80.0 75.0
shearing strength23℃ASTM D-732无水｜790 kg/cm2
Impact strength of cantilever beam gap23℃，无缺口1/83.5%水｜- kg·cm/cm2
bending strength-40°C140 MPa
-40℃ASTM D-790无水｜1450 kg/cm2
Impact strength of cantilever beam gap-40℃，V缺口1/2ASTM D-2563.5%水｜- kg·cm/cm
Flexural modulus-40℃ASTM D-7903.5%水｜42000 kg/cm2
bending strength80℃ASTM D-7903.5%水｜400 kg/cm2
compression stress23°CMPa90.0 --
Flexural modulus23℃ASTM D-7903.5%水｜14000 kg/cm2
80°CMPa900 500
tensile strength 80℃，屈服ASTM D-6383.5%水｜400 kg/cm2
-40°C115 MPa
Tensile strain屈服,23°C%1.5 --
elongation at break23℃ASTM D-6383.5%水｜< 200 %
tensile strength -40℃，屈服ASTM D-6383.5%水｜1100 kg/cm2
Charpy Notched Impact StrengthASTM D256/ISO 17950 kg·cm/cm(J/M)ft·lb/in
Flexural modulus23°CMPa2900 1400
Friction coefficient - vs. Metal0.15to0.20 --
Electrical performanceTest ConditionTest MethodTORAY JAPAN/CM3006
dielectric constant23°C,50Hz1.60 --
Compared to the Leakage Tracking Index (CTI)CTIV --
Dissipation Factor50HzASTM D-1503.5%水｜-
23°C,50Hz0.060 --
Volume resistivityASTM D-257无水｜1014-1015 Ω.cm
dielectric constant50HzASTM D-1503.5%水｜-
Compared to the Leakage Traceability Index (CTI)UL 7463.5%水｜530 V
dielectric constantASTM D150/IEC 602503.3
Volume resistivityohms·cm1.0E+13-1.0E+14 1.0E+12到1.0E+13
Physical propertiesTest ConditionTest MethodTORAY JAPAN/CM3006
densityASTM D792/ISO 11831.14
Water absorption rateASTM D570/ISO 621.2 %
flammabilityTest ConditionTest MethodTORAY JAPAN/CM3006
UL flame retardant rating0.79mmV-2 --
physical property Test ConditionTest MethodTORAY JAPAN/CM3006
Water absorption rate饱和,23°C%8.0 --
Shrinkage rateMD：1.00mm3%0.80-1.5 --
MD：3.00mm4%1.5-2.2 --
Taber abraser1000g,CS-17ASTM D-1044无水｜8 mg/1000次
Water absorption rate23°C,24hr%1.2 --
Thermal performanceTest ConditionTest MethodTORAY JAPAN/CM3006
Combustibility (rate)UL 94V-2
Heat distortion temperature0.45MPa,未退火，HDT°C220 --
thermal conductivity3.5%水｜- Kcal/m·hr·℃
melting temperature°C265 --
Linear coefficient of thermal expansionMDcm/cm/°C9.0E-5到1.0E-4 --
melting temperature差示扫描测热计DSC265 °C
specific heat3.5%水｜- Cal/g·℃
UL-94 flame retardant grade1/32"UL 943.5%水｜-
specific heatJ/kg/°C2100 --
Heat distortion temperature4.6kg/cm2，HDTASTM D-6483.5%水｜- °C
Linear coefficient of thermal expansionASTM D696/ISO 113590.32 mm/mm.℃
ASTM D-6963.5%水｜- ×10-5cm/cm/℃
Heat distortion temperatureHDTASTM D648/ISO 75220(0.46MPa) ℃（℉）
thermal conductivityW/m/K0.32 --