PC/PET X7200MR-NA9A002 SABIC INNOVATIVE US
XYLEX™
Automotive Applications、Electronic and electrical
Flame retardant、High heat resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/X7200MR-NA9A002 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 99.0 °C |
| Vicat Softening Temperature | ISO306/B120 | 115 °C | |
| Linear thermal expansion coefficient | MD：23到60°C | ISO11359-2 | 8E-05 cm/cm/°C |
| Thermal Conductivity | ISO8302 | 0.23 W/m/K | |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 96.0 °C |
| Ball PressureTest | 105°C | IEC60695-10-2 | Pass |
| Linear thermal expansion coefficient | TD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C |
| TD：23to60°C | ISO11359-2 | 8E-05 cm/cm/°C | |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 90.0 °C |
| Vicat Softening Temperature | ASTMD15259 | 115 °C | |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE US/X7200MR-NA9A002 |
|---|---|---|---|
| Shore Hardness | 邵氏D,10秒 | ASTMD2240 | 76 |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/X7200MR-NA9A002 |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 1960 Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 56.0 Mpa |
| Tensile Elongation | ASTMD638 | 140 % | |
| Tensile Strain | ISO527-2/50 | >150 % | |
| Tensile Modulus | ISO527-2/1 | 2000 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 55.0 Mpa |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 84.0 Mpa |
| Flexural Modulus | ISO178 | 2000 Mpa | |
| Tensile Elongation | 屈服 | ASTMD638 | 5.0 % |
| Tensile Stress | ISO527-2/50 | 55.0 Mpa | |
| Flexural Strength | ISO178 | 75.0 Mpa | |
| Tensile Modulus | ASTMD638 | 1880 Mpa | |
| Tensile Strength | 断裂 | 56.0 Mpa | |
| Tensile Strain | 屈服 | ISO527-2/5 | 5.0 % |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/X7200MR-NA9A002 |
|---|---|---|---|
| Melt Mass-Flow Rate | 265°C/2.16kg | ASTMD1238 | 12 g/10min |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| TD：3.20mm | 0.50to0.70 % | ||
| Melt Volume flow Rate | 265°C/2.16kg | ISO1133 | 12.0 cm3/10min |
| Optical | Test Condition | Test Method | SABIC INNOVATIVE US/X7200MR-NA9A002 |
|---|---|---|---|
| Index of Refraction | ISO489 | 1.557 | |
| Transmittance | 2540µm | ASTMD1003 | 88.0 % |
| Haze | 1.1 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/X7200MR-NA9A002 |
|---|---|---|---|
| Notched Izod Impact Strength | -10°C | ISO180/1A | 5.0 kJ/m² |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 95.0 J |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 8.0 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/X7200MR-NA9A002 |
|---|---|---|---|
| Flame Rating | 3.0mm | UL94 | V-2 |
| Glow Wire Flammability Index | 1.0mm | IEC60695-2-12 | 750 °C |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/X7200MR-NA9A002 |
|---|---|---|---|
| Surface Resistivity | ASTMD257 | >1.0E+15 ohms | |
| Volume Resistivity | >1.0E+15 ohms·cm |