TSU-Ether InnoTuf® HP-2120A Innovative Polymers, Inc.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermosetting | Test Condition | Test Method | Innovative Polymers, Inc./InnoTuf® HP-2120A |
|---|---|---|---|
| Thermosetting components | 脱模时间 | 300to420 min | |
| 硬化法 | 按容量计算的混合比:44按重量计算的混合比:43 | ||
| 树脂 | 按容量计算的混合比:100按重量计算的混合比:100 |
| Uncured Properties | Test Condition | Test Method | Innovative Polymers, Inc./InnoTuf® HP-2120A |
|---|---|---|---|
| Viscosity | GelTime | 15to25 min | |
| 25°C2 | 0.48 Pa·s | ||
| 25°C3 | 0.63 Pa·s | ||
| 25°C1 | 0.13 Pa·s | ||
| 固化时间4 | 29 hr |
| Cured Properties | Test Condition | Test Method | Innovative Polymers, Inc./InnoTuf® HP-2120A |
|---|---|---|---|
| tear strength | ASTM D624 | 5.25 kN/m | |
| elongation | 断裂 | ASTM D638 | 500 % |
| tensile strength | ASTM D638 | 1.79 MPa | |
| Shore hardness | ShoreA | ASTM D2240 | 15to25 |
| physical property | Test Condition | Test Method | Innovative Polymers, Inc./InnoTuf® HP-2120A |
|---|---|---|---|
| density | Hardener | 1.03 g/cm³ | |
| 基体树脂 | 1.06 g/cm³ | ||
| Cured | 1.04 g/cm³ | ||
| Shrinkage rate | MD | ASTM D2566 | 0.20to0.50 % |