PPA AFA-4133 V0 Z NT SOLVAY USA
AMODEL®
Electrical components、Electrical/Electronic App、Laptop case、Vehicle electronics
Filler: Glass fiber reinf、33% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SOLVAY USA/AFA-4133 V0 Z NT |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 68 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 79 kJ/m² |
| Electrical performance | Test Condition | Test Method | SOLVAY USA/AFA-4133 V0 Z NT |
|---|---|---|---|
| Dissipation Factor | 60Hz | ASTM D150 | 6E-03 |
| dielectric constant | 60Hz | ASTM D150 | 4.10 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | mm/min |
| Volume resistivity | ASTM D257 | 5.6E+15 ohms·cm | |
| Dissipation Factor | 1MHz | ASTM D150 | 0.015 |
| dielectric strength | 3.20mm | ASTM D149 | 19 KV/mm |
| dielectric constant | 1MHz | ASTM D150 | 3.75 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| Mechanical properties | Test Condition | Test Method | SOLVAY USA/AFA-4133 V0 Z NT |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.5 % |
| bending strength | 23°C | ISO 178 | 295 Mpa |
| Flexural modulus | 23°C | ISO 178 | 10700 Mpa |
| Bending Strain | ISO 178 | 3.1 % | |
| Tensile modulus | 23°C | ISO 527-2 | 12000 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 210 Mpa |
| flammability | Test Condition | Test Method | SOLVAY USA/AFA-4133 V0 Z NT |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SOLVAY USA/AFA-4133 V0 Z NT |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.40 % |
| Water absorption rate | 24hr | ASTM D570 | 0.23 % |
| Shrinkage rate | TD | ASTM D955 | 0.80 % |
| Thermal performance | Test Condition | Test Method | SOLVAY USA/AFA-4133 V0 Z NT |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 327 °C | |
| Linear coefficient of thermal expansion | TD：100到200°C | ASTME831 | 1.2E-04 cm/cm/°C |
| Glass Transition Temperature | DSC | 95.0 °C | |
| Linear coefficient of thermal expansion | MD：100到200°C | ASTME831 | 1.5E-05 cm/cm/°C |
| TD：0to100°C | ASTME831 | 7.6E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | >300 °C |
| Linear coefficient of thermal expansion | MD：0to100°C | ASTME831 | 2E-05 cm/cm/°C |