| Impact resistance | Test Condition | Test Method | CHI MEI CORPORATION/WONDERLITE® PC-175 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 10 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 8.0 kJ/m² |
| hardness | Test Condition | Test Method | CHI MEI CORPORATION/WONDERLITE® PC-175 |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 77 |
| Mechanical properties | Test Condition | Test Method | CHI MEI CORPORATION/WONDERLITE® PC-175 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 70 % |
| Flexural modulus | ASTM D790 | 2340 MPa | |
| tensile strength | 屈服 | ASTM D638 | 61.6 MPa |
| Flexural modulus | ISO 178 | 2400 MPa | |
| bending strength | ASTM D790 | 89.8 MPa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 65 % |
| bending strength | ISO 178 | 90.0 MPa | |
| tensile strength | 屈服 | ISO 527-2/50 | 60.0 MPa |
| 断裂 | ISO 527-2/50 | 50.0 MPa |
| physical property | Test Condition | Test Method | CHI MEI CORPORATION/WONDERLITE® PC-175 |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.20 g/cm³ |
| Shrinkage rate | ISO 294-4 | 0.50to0.70 % | |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 65.0 cm³/10min |
| density | ASTM D792 | 1.20 g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 62 g/10min |
| Thermal performance | Test Condition | Test Method | CHI MEI CORPORATION/WONDERLITE® PC-175 |
|---|---|---|---|
| vicat | ASTM D15256 | 150 °C | |
| -- | ISO 306/A50 | 145 °C | |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 140 °C |
| vicat | -- | ISO 306/B50 | 140 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 124 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6.0E-5to8.0E-5 cm/cm/°C |