Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPA HTNFR52G45NHLW DUPONT USA
Zytel®
household electrical appl、Automotive interior parts、electrical equipment
Dimensional stability、Low water absorption、Heat aging、high strength、High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/HTNFR52G45NHLW |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 48 kJ/m² |
| -30°C | ISO 179/1eU | 45 kJ/m² |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/HTNFR52G45NHLW |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 15500 Mpa | |
| bending strength | ISO 178 | 249 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 1.7 % |
| Flexural modulus | ISO 178 | 15100 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 167 Mpa |
| Electrical performance | Test Condition | Test Method | DUPONT USA/HTNFR52G45NHLW |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| Dissipation Factor | 100 Hz | IEC 62631-2-1 | 6.0E-3 |
| 1 MHz | IEC 62631-2-1 | 0.012 | |
| dielectric strength | IEC 60243-1 | 40 KV/mm | |
| Volume resistivity | IEC 62631-3-1 | > 1.0E+13 ohms·m | |
| relative permittivity | 1 MHz | IEC 62631-2-1 | 4.40 |
| 100 Hz | IEC 62631-2-1 | 4.70 |
| flammability | Test Condition | Test Method | DUPONT USA/HTNFR52G45NHLW |
|---|---|---|---|
| Hot filament ignition temperature | 1.5 mm | IEC 60695-2-13 | 750 °C |
| Burning wire flammability index | 0.75 mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 3.0 mm | IEC 60695-2-13 | 800 °C |
| UL flame retardant rating | UL 94 | V-0 | |
| Hot filament ignition temperature | 0.40 mm | IEC 60695-2-13 | 700 °C |
| Burning wire flammability index | 3.0 mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 0.75 mm | IEC 60695-2-13 | 750 °C |
| Burning wire flammability index | 1.5 mm | IEC 60695-2-12 | 960 °C |
| 0.40 mm | IEC 60695-2-12 | 960 °C |
| physical property | Test Condition | Test Method | DUPONT USA/HTNFR52G45NHLW |
|---|---|---|---|
| Shrinkage rate | 流量 | ISO 294-4 | 0.20 % |
| 横向流量 | ISO 294-4 | 0.60 % |
| Thermal performance | Test Condition | Test Method | DUPONT USA/HTNFR52G45NHLW |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 310 °C | |
| Linear coefficient of thermal expansion | 横向 : -40 到 23°C | ISO 11359-2 | 4.3E-5 cm/cm/°C |
| RTI Elec | 0.40 mm | UL 746 | 140 °C |
| Linear coefficient of thermal expansion | 流动 : -40 到 23°C | ISO 11359-2 | 1.3E-5 cm/cm/°C |
| RTI Elec | 0.75 mm | UL 746 | 140 °C |
| 3.0 mm | UL 746 | 140 °C | |
| Linear coefficient of thermal expansion | 流动 : 55 到 160°C | ISO 11359-2 | 1.4E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 284 °C |
| Linear coefficient of thermal expansion | 横向 : 55 到 160°C | ISO 11359-2 | 8.0E-5 cm/cm/°C |
| 流动 | ISO 11359-2 | 1.5E-5 cm/cm/°C | |
| 横向 | ISO 11359-2 | 5.0E-5 cm/cm/°C | |
| RTI Elec | 1.5 mm | UL 746 | 140 °C |
| injection | Test Condition | Test Method | DUPONT USA/HTNFR52G45NHLW |
|---|---|---|---|
| Temperature | Drying Recommended | yes | |
| Suggested maximum moisture content | 0.10 % | ||
| Drying time - hot air dryer | 6.0 to 8.0 hr | ||
| Processing (melt) temperature | 320 to 325 °C | ||
| drying temperature | 100 °C | ||
| Temperature | 90 to 130 °C |