PPO N190X-71283 SABIC INNOVATIVE SHANGHAI

NORYL™

Automotive components,Illuminating lamp

transparent,High temperature resistan

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

hardness	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/N190X-71283
Rockwell hardness	R-Scale	ASTM D785	120

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/N190X-71283
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	95.0 °C
		1.8 MPa, Unannealed, 3.20 mm	ASTM D648	78.0 °C
		1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8	ISO 75-2/Af	82.0 °C
		0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span8	ISO 75-2/Bf	95.0 °C
		1.8 MPa, Unannealed, 6.40 mm	ASTM D648	86.0 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.7E-5 cm/cm/°C
Linear coefficient of thermal expansion		Across Flow : -40 to 40°C	ASTM E831	8.1E-5 cm/cm/°C
RTI		UL 746	95.0 °C
RTI Elec		UL 746	95.0 °C
RTI Imp		UL 746	80.0 °C
thermal conductivity		ASTM C177	0.24 W/m/K
Vicat softening temperature	--	ISO 306/B120	107 °C
Vicat softening temperature		--	ASTM D15259	104 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/N190X-71283
Bending modulus	--6	ISO 178	2350 Mpa
		100 mm Span5	ASTM D790	2300 Mpa
		50.0 mm Span4	ASTM D790	2500 Mpa
bending strength	Yield, 50.0 mm Span4	ASTM D790	98.0 Mpa
		--6,7	ISO 178	87.0 Mpa
		Yield, 100 mm Span5	ASTM D790	91.0 Mpa
elongation	Yield	ISO 527-2/50	3.2 %
		Yield3	ASTM D638	3.6 %
		Break3	ASTM D638	9.0 %
		Break	ISO 527-2/50	9.2 %
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	ASTM D1044	76.0 mg
Tensile modulus	--2	ASTM D638	2580 Mpa
Tensile modulus		--	ISO 527-2/1	2600 Mpa
tensile strength	Yield	ISO 527-2/50	58.0 Mpa
		Break	ISO 527-2/50	50.0 Mpa
		Break3	ASTM D638	47.0 Mpa
		Yield3	ASTM D638	60.0 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/N190X-71283
Arc resistance		ASTM D495	PLC 7
Compared to the anti leakage trace index		UL 746	PLC 1
Dielectric constant	100 kHz	ASTM D150	2.60
Dielectric constant		100 Hz	ASTM D150	2.74
Dielectric strength	3.20 mm, in Oil	ASTM D149	19 KV/mm
Dissipation factor	100 kHz	ASTM D150	5.5E-3
Dissipation factor		100 Hz	ASTM D150	0.013
High arc combustion index		UL 746	PLC 2
High voltage arc tracing rate		UL 746	PLC 4
Hot wire ignition		UL 746	PLC 2
Volume resistivity		ASTM D257	1.8E+16 ohms·cm

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/N190X-71283
melt mass-flow rate	280°C/5.0 kg	ASTM D1238	20 g/10 min
Melt Volume Flow Rate (MVR)	280°C/5.0 kg	ISO 1133	23.0 cm3/10min
Outdoor applicability		UL 746C	f1
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70 %
Water absorption rate	24 hr	ASTM D570	0.080 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/N190X-71283
Dart impact	23°C, Total Energy	ASTM D3763	50.0 J
Suspended wall beam without notch impact strength	23°C	ASTM D4812	720 J/m

flammability	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/N190X-71283
Extreme Oxygen Index		ASTM D2863	39 %
UL flame retardant rating	3.0 mm	UL 94	5VA
		1.0 mm	UL 94	HB
		1.5 mm	UL 94	V-0

injection	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/N190X-71283
Back pressure			0.300 to 0.700 Mpa
drying temperature			75 to 80 °C
drying time			3.0 to 4.0 hr
Exhaust hole depth			0.038 to 0.051 mm
Mold temperature			55 to 75 °C
Processing (melt) temperature			250 to 275 °C
Screw speed			20 to 100 rpm
Spray nozzle temperature			250 to 275 °C
Suggested injection volume			30 to 70 %
Suggested maximum moisture content			0.020 %
Temperature at the front of the material cylinder			240 to 275 °C
Temperature at the rear of the barrel			215 to 265 °C
Temperature in the middle of the barrel			225 to 270 °C