PC/PET X7200-NA9A002 SABIC EU

XYLEX™

Industrial applications,Electronic field,Electrical field,Automotive sector

High mobility,UV resistance

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

thermal performance	Test Condition	Test Method	SABIC EU/X7200-NA9A002
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	71.1 °C
		1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	73.4 °C
		0.45MPa,Unannealed,3.20mm	ASTM D648	110 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	9.9E-05 cm/cm/°C
		TD：-40to40°C	ISO 11359-2	1.1E-04 cm/cm/°C
		TD：-40to40°C	ASTME831	1.1E-04 cm/cm/°C
		MD：-40to40°C	ISO 11359-2	9.9E-05 cm/cm/°C
Vicat softening temperature	--	ISO 306/B120	107 °C
			ASTM D152510	146 °C
		--	ISO 306/B50	103 °C

mechanical properties	Test Condition	Test Method	SABIC EU/X7200-NA9A002
Bending modulus	50.0mmSpan	ASTM D790	1450 Mpa
Bending modulus			ISO 178	1610 Mpa
bending strength	Yield,50.0mmSpan	ASTM D790	49.0 Mpa
bending strength			ISO 178	48.0 Mpa
elongation	Break	ASTM D638	130 %
elongation		Yield	ASTM D638	10 %
Tensile modulus		ASTM D638	1240 Mpa
Tensile modulus			ISO 527-2/1	1670 Mpa
Tensile strain	Break	ISO 527-2/50	120 %
Tensile strain		Yield	ISO 527-2/50	8.2 %
tensile strength	Yield	ASTM D638	33.8 Mpa
		Yield	ISO 527-2/50	34.0 Mpa
		Break	ISO 527-2/50	28.0 Mpa
		Break	ASTM D638	27.6 Mpa

Physical properties	Test Condition	Test Method	SABIC EU/X7200-NA9A002
melt mass-flow rate	260°C/5.0kg	ASTM D1238	16 g/10min
Melt Volume Flow Rate (MVR)	260°C/5.0kg	ISO 1133	18.0 cm3/10min
Shrinkage rate	TD：3.20mm	Internal Method	0.60-0.80 %
Shrinkage rate		MD：3.20mm	Internal Method	0.60-0.80 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.020 %
Water absorption rate		Saturation,23°C	ISO 62	0.050 %

impact performance	Test Condition	Test Method	SABIC EU/X7200-NA9A002
Charpy Notched Impact Strength	23°C	ISO 179/1eA	12 kJ/m²
Charpy Notched Impact Strength		-30°C	ISO 179/1eA	6.1 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	36.2 J
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	8.0 kJ/m²
Impact strength of cantilever beam gap		23°C	ISO 180/1A	14 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	80 kJ/m²
Impact strength of simply supported beam without notch		23°C	ISO 179/1eU	NoBreak
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	NoBreak
Suspended wall beam without notch impact strength		23°C	ISO 180/1U	NoBreak