LCP A625 CELANESE USA
VECTRA®
Fitness equipment、Home appliance components、Automotive Applications
Halogen-free、Flame retardant、wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CELANESE USA/A625 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 62 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 67 kJ/m² |
| hardness | Test Condition | Test Method | CELANESE USA/A625 |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 62 |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/A625 |
|---|---|---|---|
| Tensile creep modulus | 1hr | ISO 899-1 | 9800 Mpa |
| Tensile modulus | ISO 527-2/1A/1 | 9000 Mpa | |
| bending strength | 23°C | ISO 178 | 140 Mpa |
| Compression Modulus | ISO 604 | 9000 Mpa | |
| Tensile creep modulus | 1000hr | ISO 899-1 | 7500 Mpa |
| Flexural modulus | 23°C | ISO 178 | 10500 Mpa |
| Compressive Stress | 1%Strain | ISO 604 | 56.0 Mpa |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 140 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 5.7 % |
| Electrical performance | Test Condition | Test Method | CELANESE USA/A625 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| Volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 30.0 |
| Dissipation Factor | 100Hz | IEC 60250 | 0.040 |
| relative permittivity | 1MHz | IEC 60250 | 13.0 |
| Surface Resistivity | IEC 60093 | 1E+11 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.15 |
| flammability | Test Condition | Test Method | CELANESE USA/A625 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| physical property | Test Condition | Test Method | CELANESE USA/A625 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.50 % |
| MD | ISO 294-4 | 0.10 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.030 % |
| Thermal performance | Test Condition | Test Method | CELANESE USA/A625 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 280 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 225 °C |
| vicat | ISO 306/B50 | 159 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 185 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 9E-06 cm/cm/°C |
| Heat distortion temperature | 8.0MPa,未退火，HDT | ISO 75-2/C | 114 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 3E-05 cm/cm/°C |