PPA UF1008HS-NS SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Automotive components
Toughening、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/UF1008HS-NS |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 14300 Mpa | |
| bending strength | ISO 178 | 322 Mpa | |
| Flexural modulus | ISO 178 | 13800 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 205 Mpa |
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 9.0 kJ/m² |
| elongation | 断裂 | ISO 527-2 | 2.0 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/UF1008HS-NS |
|---|---|---|---|
| Water absorption rate | 23℃， 24hr | ISO 62 | 0.42 % |
| Shrinkage rate | MD | ISO 294-4 | 0.27 % |
| 横向 | ISO 294-4 | 1.2 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/UF1008HS-NS |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，64mm，HDT | ISO 75-2/Af | 272 °C |
| 1.8MPa,未退火，3.2mm，HDT | ASTM D648 | 282 °C |