PA6 Polifil® Nylon 930L 美国The Plastics
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 美国The Plastics/Polifil® Nylon 930L |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 59 J/m |
| Dart impact | 23°C,12.7mm | ASTM D3029 | 1.36 J |
| hardness | Test Condition | Test Method | 美国The Plastics/Polifil® Nylon 930L |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 116 |
| Mechanical properties | Test Condition | Test Method | 美国The Plastics/Polifil® Nylon 930L |
|---|---|---|---|
| bending strength | 23°C | ASTM D790 | 103 MPa |
| tensile strength | 23°C | ASTM D638 | 79.3 MPa |
| Tensile modulus | 23°C | ASTM D638 | 3030 MPa |
| Flexural modulus | 23°C | ASTM D790 | 2690 MPa |
| elongation | 屈服,23°C | ASTM D638 | 8.0 % |
| 断裂,23°C | ASTM D638 | 40 % |
| physical property | Test Condition | Test Method | 美国The Plastics/Polifil® Nylon 930L |
|---|---|---|---|
| Water absorption rate | 24hr | ASTM D570 | 1.6 % |
| density | ASTM D792 | 1.13 g/cm³ | |
| Shrinkage rate | MD：3.18mm | ASTM D955 | 1.2 % |
| Thermal performance | Test Condition | Test Method | 美国The Plastics/Polifil® Nylon 930L |
|---|---|---|---|
| Hot deformation temperature (HDT) | 1.8MPa,未退火，HDT | ASTM D648 | 62.8 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 182 °C |