PPO 9406P-701 SABIC INNOVATIVE NANSHA
NORYL™
Electrical applications、electrical equipment
High mobility、Chemical resistance、High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/9406P-701 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 11 kJ/m² |
Dart impact | 23°C,TotalEnergy | ASTM D3763 | 52.0 J |
Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 8.0 kJ/m² |
Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 8.0 kJ/m² |
23°C | ISO 180/1A | 10 kJ/m² |
Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/9406P-701 |
---|---|---|---|
bending strength | 屈服,50.0mm跨距4 | ASTM D790 | 113 Mpa |
Tensile modulus | ISO 527-2/1 | 2730 Mpa | |
elongation | 屈服 | ASTM D638 | 4.7 % |
tensile strength | 断裂 | ASTM D638 | 55.0 Mpa |
Flexural modulus | 50.0mm跨距4 | ASTM D790 | 2840 Mpa |
Tensile strain | 屈服 | ISO 527-2/50 | 4.7 % |
tensile strength | 断裂 | ISO 527-2/50 | 55.0 Mpa |
bending strength | Yield,6.40mm | ASTM D790 | 114 Mpa |
tensile strength | 屈服 | ISO 527-2/50 | 76.0 Mpa |
Flexural modulus | 6.40mm | ASTM D790 | 2840 Mpa |
Tensile modulus | ASTM D638 | 2800 Mpa | |
elongation | 断裂 | ASTM D638 | 9.7 % |
bending strength | ISO 178 | 114 Mpa | |
Flexural modulus | ISO 178 | 2580 Mpa | |
tensile strength | 屈服 | ASTM D638 | 76.0 Mpa |
Tensile strain | 断裂 | ISO 527-2/50 | 9.4 % |
Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/9406P-701 |
---|---|---|---|
Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 4 |
flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/9406P-701 |
---|---|---|---|
UL flame retardant rating | 0.75mm | UL 94 | V-0 |
2.5mm | UL 94 | 5VA | |
2.0mm | UL 94 | 5VB | |
Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 775 °C |
Burning wire flammability index | 0.75mm | IEC 60695-2-12 | 960 °C |
Hot filament ignition temperature | 0.8mm | IEC 60695-2-13 | 750 °C |
physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/9406P-701 |
---|---|---|---|
Melt volume flow rate | 280°C/5.0kg | ISO 1133 | 10.0 cm3/10min |
Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/9406P-701 |
---|---|---|---|
Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan,HDT | ISO 75-2/Bf | 133 °C |
1.8MPa,未退火,6.40mm,HDT | ASTM D648 | 122 °C | |
vicat | -- | ISO 306/B120 | 140 °C |
-- | ISO 306/A120 | 150 °C | |
Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan,HDT | ISO 75-2/Af | 118 °C |
RTI Imp | UL 746 | 105 °C | |
RTI Str | UL 746 | 110 °C | |
Heat distortion temperature | 1.8MPa,未退火,3.20mm,HDT | ASTM D648 | 118 °C |
ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
RTI Elec | UL 746 | 110 °C |