PA66 HTNFR52G20LX NC010 DUPONT USA
Zytel®
Electronic and electrical components
Flame retardant,High temperature resistan,Filler: Glass fiber reinf,20% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | DUPONT USA/HTNFR52G20LX NC010 |
|---|---|---|---|
| Hot deformation temperature | 1.8MPa,未退火 | °C | 276 -- |
| Linear coefficient of thermal expansion | TD | cm/cm/°C | 6.8E-05 -- |
| TD:55到160°C | cm/cm/°C | 1E-04 -- | |
| MD:-40到23°C | cm/cm/°C | 2.7E-05 -- | |
| MD | cm/cm/°C | 2.5E-05 -- | |
| MD:55到160°C | cm/cm/°C | 2.1E-05 -- | |
| TD:-40到23°C | cm/cm/°C | 6.4E-05 -- | |
| Melting temperature | °C | 310 -- |
| mechanical properties | Test Condition | Test Method | DUPONT USA/HTNFR52G20LX NC010 |
|---|---|---|---|
| Bending modulus | MPa | 7800 8200 | |
| bending strength | MPa | 215 180 | |
| Tensile modulus | 8200 MPa | ||
| Tensile strain | 断裂 | % | 2.4 2.2 |
| tensile strength | 断裂 | 135 MPa |
| Electrical performance | Test Condition | Test Method | DUPONT USA/HTNFR52G20LX NC010 |
|---|---|---|---|
| Compared to the anti leakage trace index | V | PLC 0 | |
| Dielectric strength | kV/mm | 42 -- | |
| Volume resistivity | ohms·cm | >1.0E+15 -- |
| Physical properties | Test Condition | Test Method | DUPONT USA/HTNFR52G20LX NC010 |
|---|---|---|---|
| Shrinkage rate | TD | % | 1.1 -- |
| MD | % | 0.30 -- |
| impact performance | Test Condition | Test Method | DUPONT USA/HTNFR52G20LX NC010 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | kJ/m² | 40 |
| 23°C | kJ/m² | 40 |
| flammability | Test Condition | Test Method | DUPONT USA/HTNFR52G20LX NC010 |
|---|---|---|---|
| Burning wire flammability index | 0.400mm | °C | 960 -- |
| Extreme Oxygen Index | % | 35 -- | |
| Flammability level | 0.750mm | V-0 -- | |
| 1.50mm | V-0 -- | ||
| Hot filament ignition temperature | 0.400mm | °C | 725 -- |