LDPE Polymer-E F2200 Asia Polymer Corporation (APC)
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | Asia Polymer Corporation (APC)/Polymer-E F2200 |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 52 |
| film | Test Condition | Test Method | Asia Polymer Corporation (APC)/Polymer-E F2200 |
|---|---|---|---|
| tensile strength | TD:断裂 | ASTM D882 | 15.7 MPa |
| Elmendorf tear strength | MD | ASTM D1922 | 100000 g |
| Dart impact | ASTM D1709 | 92 g | |
| elongation | MD:断裂 | ASTM D882 | 300 % |
| Secant modulus | 1%正割,TD | ASTM D882 | 191 MPa |
| Elmendorf tear strength | TD | ASTM D1922 | 64000 g |
| tensile strength | MD:断裂 | ASTM D882 | 24.5 MPa |
| elongation | TD:断裂 | ASTM D882 | 510 % |
| Secant modulus | 1%正割,MD | ASTM D882 | 181 MPa |
| Mechanical properties | Test Condition | Test Method | Asia Polymer Corporation (APC)/Polymer-E F2200 |
|---|---|---|---|
| coefficient of friction | ASTM D1894 | >0.50 |
| optical performance | Test Condition | Test Method | Asia Polymer Corporation (APC)/Polymer-E F2200 |
|---|---|---|---|
| Haze ratio | 31.8µm,吹塑薄膜 | ASTM D1003 | 4.6 % |
| gloss | 31.8µm,吹塑薄膜 | ASTM D523 | 122 |
| physical property | Test Condition | Test Method | Asia Polymer Corporation (APC)/Polymer-E F2200 |
|---|---|---|---|
| density | ASTM D1505 | 0.922 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 2.3 g/10min |
| Thermal performance | Test Condition | Test Method | Asia Polymer Corporation (APC)/Polymer-E F2200 |
|---|---|---|---|
| vicat | ASTM D1525 | 96.0 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 48.0 °C |
| brittle temperature | ASTM D746 | <-70.0 °C |