PA66 RFL-4033 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electrical appliances、Electronic and Electrical
wear resistant、enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/RFL-4033 |
|---|---|---|---|
| Linear thermal expansion coefficient | TD：-40到40°C | ISO11359-2 | 3.9E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 261 °C |
| Linear thermal expansion coefficient | TD：-40到40°C | ASTME831 | 4E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 260 °C |
| Linear thermal expansion coefficient | MD：-40到40°C | ISO11359-2 | 8.3E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 247 °C |
| 1.8MPa,未退火,64.0mm跨距 | ISO75-2/Af | 243 °C | |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 8.3E-05 cm/cm/°C |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/RFL-4033 |
|---|---|---|---|
| Tensile Strain | 屈服 | ISO527-2 | 3.1 % |
| Tensile Elongation | 断裂 | ASTMD638 | 3.1 % |
| Flexural Modulus | ASTMD790 | 5520 Mpa | |
| Flexural Strength | 179 Mpa | ||
| Tensile Stress | 屈服 | ISO527-2 | 118 Mpa |
| Coefficient of Friction | Dynamic | ASTMD3702Modified | 0.40 |
| Tensile Modulus | ISO527-2/1 | 6440 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 120 Mpa |
| Flexural Modulus | ISO178 | 5800 Mpa | |
| Coefficient of Friction | Static | ASTMD3702Modified | 0.45 |
| Tensile Elongation | 屈服 | ASTMD638 | 3.1 % |
| Specific Wear Rate | ASTMD3702Modified | 19.5 10^-10in^5-min/ft-lb-hr | |
| Tensile Strain | 断裂 | ISO527-2 | 3.1 % |
| Tensile Stress | 118 Mpa | ||
| Flexural Stress | ISO178 | 183 Mpa | |
| Tensile Modulus | ASTMD638 | 6890 Mpa | |
| Tensile Strength | 断裂 | 120 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/RFL-4033 |
|---|---|---|---|
| Moisture Absorption | 24hr,50%RH | ASTMD570 | 0.60 % |
| Modeling Shrinkage | MD：24小时 | ASTMD955 | 0.50to0.70 % |
| TD：24hr | 1.6to1.8 % | ||
| TD:24小时 | ISO294-4 | 1.7 % | |
| MD:24小时 | 0.64 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/RFL-4033 |
|---|---|---|---|
| Instrumented Dart Impact | 23°C,EnergyatPeakLoad | ASTMD3763 | 7.60 J |
| 23°C | ISO180/1U | 35 kJ/m² | |
| Notched Izod Impact Strength | ISO180/1A | 6.7 kJ/m² | |
| Multi-Axial Instrumented Impact Energy | ISO6603-2 | 2.10 J |