HDPE B5429 SABIC SAUDI
SABIC®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | SABIC SAUDI/B5429 |
---|---|---|---|
Impact strength of cantilever beam gap | -30°C,模压成型 | ISO 180/A | 5.0 kJ/m² |
23°C,模压成型 | ISO 180/A | 12 kJ/m² |
hardness | Test Condition | Test Method | SABIC SAUDI/B5429 |
---|---|---|---|
Shore hardness | 邵氏D,模压成型 | ISO 868 | 61 |
Supplementary Information | Test Condition | Test Method | SABIC SAUDI/B5429 |
---|---|---|---|
Blow molding melt temperature | 165to215 °C |
Mechanical properties | Test Condition | Test Method | SABIC SAUDI/B5429 |
---|---|---|---|
Tensile strain | 断裂,2.00mm,模压成型 | ISO 527-2/1BA/50 | >1000 % |
bending strength | 2.00mm,模压成型 | ISO 178 | 27.0 Mpa |
Tensile modulus | 2.00mm,模压成型 | ISO 527-2/1BA/50 | 1050 Mpa |
tensile strength | 屈服,2.00mm,模压成型 | ISO 527-2/1BA/50 | 26.0 Mpa |
断裂,2.00mm,模压成型 | ISO 527-2/1BA/50 | 28.0 Mpa | |
Flexural modulus | 2.00mm,模压成型 | ISO 178 | 1250 Mpa |
physical property | Test Condition | Test Method | SABIC SAUDI/B5429 |
---|---|---|---|
melt mass-flow rate | 190°C/5.0kg | ISO 1133 | 1.5 g/10min |
density | ISO 1183 | 0.954 g/cm³ | |
melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 0.30 g/10min |
190°C/21.6kg | ISO 1133 | 29 g/10min | |
Environmental stress cracking resistance | 10%IgepalCO-630,模压成型,F50 | ASTM D1693B | 40.0 hr |
Thermal performance | Test Condition | Test Method | SABIC SAUDI/B5429 |
---|---|---|---|
Heat distortion temperature | 0.45MPa,未退火,HDT | ASTM D648 | 81.0 °C |
vicat | ASTM D15252 | 127 °C | |
melting temperature | DIN 53765 | 132 °C | |
EnthalpyChange | DIN 53765 | 205 J/g |