Material Comparison

Product Info

Product Name

Brand Name

Usages

Properties

Certificates

PP AP03B EXXONMOBIL SINGAPORE

ExxonMobil™

Industrial applications、Home appliance components、Automotive sector、Automotive interior parts、Consumer goods sector、Application in the automo、Consumer product applicat

High impact resistance、High mobility、Easy to process、High crystallinity、High rigidity、Fast forming cycle

TDS

Plastic Datasheets

Impact resistance	Test Condition	Test Method	EXXONMOBIL SINGAPORE/AP03B
Charpy Notched Impact Strength	23°C	ISO 179/1eA	7.6 kJ/m²
		-30°C	ISO 179/1eA	3.4 kJ/m²
		-20°C	ISO 179/1eA	3.8 kJ/m²
Dart impact	-29°C,3.18mm	ASTM D5420	17.3 J
Impact strength of cantilever beam gap	23°C	ISO 180/1A	7.9 kJ/m²
Impact strength of cantilever beam gap		-40°C	ISO 180/1A	2.9 kJ/m²
Charpy Notched Impact Strength	0°C	ISO 179/1eA	4.2 kJ/m²
Impact strength of cantilever beam gap	-18°C	ASTM D256A	34 J/m
		23°C	ASTM D256A	72 J/m
		-18°C	ISO 180/1A	4.1 kJ/m²

hardness	Test Condition	Test Method	EXXONMOBIL SINGAPORE/AP03B
Rockwell hardness		ASTM D785	95

Mechanical properties	Test Condition	Test Method	EXXONMOBIL SINGAPORE/AP03B
Tensile modulus		ISO 527-2/1	1440 Mpa
tensile strength	屈服	ISO 527-2/50	25.1 Mpa
Flexural modulus	1%正割5	ASTM D790B	1500 Mpa
tensile strength	屈服3	ASTM D638	26.6 Mpa
elongation	屈服	ISO 527-2/50	4.9 %
elongation		屈服3	ASTM D638	5.0 %
Flexural modulus	--6	ISO 178	1260 Mpa
Flexural modulus		1%正割4	ASTM D790A	1310 Mpa

physical property	Test Condition	Test Method	EXXONMOBIL SINGAPORE/AP03B
melt mass-flow rate	230°C/2.16kg	ASTM D1238	30 g/10min

Thermal performance	Test Condition	Test Method	EXXONMOBIL SINGAPORE/AP03B
Heat distortion temperature	0.45MPa,未退火，HDT	ASTM D648	105 °C
		1.8MPa,未退火，HDT	ISO 75-2/A	54.6 °C
		0.45MPa,退火，HDT	ASTM D648	119 °C
		0.45MPa,未退火，HDT	ISO 75-2/Bf	93.5 °C