PA66 K224-G6 DSM HOLAND
Akulon® 
Insulation material,Shell,furniture,wheel
Glass fiber reinforced,Filler: Glass fiber reinf,30%,Filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

thermal performanceTest ConditionTest MethodDSM HOLAND/K224-G6
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B220 °C
1.8MPa,UnannealedISO 75-2/A200 °C
Linear coefficient of thermal expansionTDISO 11359-27E-05 cm/cm/°C
MDISO 11359-22E-05 cm/cm/°C
Melting temperatureISO 11357-3220 °C
mechanical propertiesTest ConditionTest MethodDSM HOLAND/K224-G6
Bending modulusISO 1788600 Mpa
bending strengthISO 178235 Mpa
Tensile modulusISO 527-29500 Mpa
Tensile strainBreakISO 527-23.5 %
tensile strengthBreakISO 527-2180 Mpa
Electrical performanceTest ConditionTest MethodDSM HOLAND/K224-G6
Compared to the anti leakage trace indexIEC 60112 V
Dielectric strengthIEC 60243-130 KV/mm
Dissipation factor1MHzIEC 602500.015
100HzIEC 602505E-03
Relative permittivity100HzIEC 602503.50
1MHzIEC 602503.30
Surface resistivityIEC 60093-- ohms
Volume resistivityIEC 600931E+15 ohms·cm
Physical propertiesTest ConditionTest MethodDSM HOLAND/K224-G6
Shrinkage rateMDISO 294-40.30 %
TDISO 294-40.90 %
Water absorption rateEquilibrium,23°C,50%RHISO 621.9 %
Saturation,23°CISO 626.3 %
impact performanceTest ConditionTest MethodDSM HOLAND/K224-G6
Impact strength of simply supported beam without notch-30°CISO 179/1eU75 kJ/m²
23°CISO 179/1eU90 kJ/m²
flammabilityTest ConditionTest MethodDSM HOLAND/K224-G6
Burning wire flammability index1.5mmIEC 60695-2-12700 °C
2.0mmIEC 60695-2-12700 °C
Hot filament ignition temperature2.0mmIEC 60695-2-13725 °C
1.5mmIEC 60695-2-13725 °C
UL flame retardant rating0.75mmIEC 60695-11-10,-20HB
1.5mmIEC 60695-11-10,-20HB