Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO ZX08309 SABIC INNOVATIVE SHANGHAI
LNP™ THERMOCOMP™
Automotive interior parts、Electrical applications
High temperature resistan、High mobility、Glass fiber reinforced、Filler: Mineral filler
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/ZX08309 |
|---|---|---|---|
| Dissipation Factor | 1.10GHz | ASTMES7-83 | 2.0E-3到4.0E-3 |
| dielectric constant | 1.10GHz | ASTMES7-83 | 4.40to4.60 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/ZX08309 |
|---|---|---|---|
| Flexural modulus | ISO 178 | 3200to3500 Mpa | |
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 90.0to100 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/ZX08309 |
|---|---|---|---|
| Melt volume flow rate | 300°C/5.0kg | ISO 1133 | 11.0 cm3/10min |
| Shrinkage rate | TD:24小时 | ASTM D955 | 0.65 % |
| MD:24小时 | ASTM D955 | 0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/ZX08309 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 134 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 122 °C |
Contact Us
Get App