Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS GSM UMG JAPAN
UMG ABS®
sporting goods
High rigidity、High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | UMG JAPAN/GSM |
|---|---|---|---|
| melt mass-flow rate | 220℃/10.0kg | ISO 1133 | 9.00 cm3/10min |
| density | ISO 1183 | 1.05 g/cm³ |
| Mechanical properties | Test Condition | Test Method | UMG JAPAN/GSM |
|---|---|---|---|
| Tensile stress | 23℃，屈服 | ISO 527-2 | 46.0 Mpa |
| Rockwell hardness | 23℃ | ISO 2039-2 | 104 R scale |
| Flexural modulus | 23℃ | ISO 178 | 2300 Mpa |
| Charpy Notched Impact Strength | -30℃ | ISO 179 | 10.00 kJ/m² |
| Tensile modulus | 23℃ | ISO 527-2 | 2150 Mpa |
| Charpy Notched Impact Strength | 23℃ | ISO 179 | 22.0 kJ/m² |
| bending strength | 23℃ | ISO 178 | 71.0 Mpa |
| Physical properties | Test Condition | Test Method | UMG JAPAN/GSM |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.05 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 0.549 g/10min |
| physical property | Test Condition | Test Method | UMG JAPAN/GSM |
|---|---|---|---|
| Shrinkage rate | Flow,23℃ | ISO 294-4 | 0.50-0.70 % |
| Thermal performance | Test Condition | Test Method | UMG JAPAN/GSM |
|---|---|---|---|
| Linear coefficient of thermal expansion | Flow | ISO 11359-2 | 0.000090 cm/cm/℃ |
| Heat distortion temperature | 1.80MPa，未退火，HDT | ISO 75-2/Af | 79.0 °C |
| UL flame retardant rating | 1.50mm | UL 94 | HB |