Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PBT 1731J-1001 SABIC INNOVATIVE THAILAND
XENOY™
medical care、Plastic bag、Gears、Automotive Applications
Chemical resistance、High impact resistance、High mobility、UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/1731J-1001 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 65 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 61.1 J |
| -30°C,TotalEnergy | ASTM D3763 | 61.5 J | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 16 kJ/m² |
| 23°C | ISO 180/1A | 59 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/1731J-1001 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2330 Mpa | |
| elongation | 屈服 | ASTM D638 | 5.0 % |
| tensile strength | 断裂 | ASTM D638 | 56.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 5.0 % |
| tensile strength | 断裂 | ISO 527-2/50 | 58.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2340 Mpa |
| Tensile modulus | ASTM D638 | 2370 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 60.0 Mpa |
| elongation | 断裂 | ASTM D638 | 100 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 93.1 Mpa |
| ISO 178 | 93.0 Mpa | ||
| Flexural modulus | ISO 178 | 2210 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 61.4 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 90 % |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/1731J-1001 |
|---|---|---|---|
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 2 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 2 |
| arc resistance | ASTM D495 | PLC 5 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/1731J-1001 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/1731J-1001 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| melt mass-flow rate | 250°C/5.0kg | ISO 1133 | 8.0 g/10min |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.60-0.80 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.080 % |
| 饱和,23°C | ISO 62 | 0.28 % | |
| Specific volume | ASTM D792 | 0.820 cm³/g | |
| melt mass-flow rate | 250°C/5.0kg | ASTM D1238 | 9.6 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/1731J-1001 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 107 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ISO 11359-2 | 7.6E-05 cm/cm/°C |
| MD：-40到95°C | ASTME831 | 8.3E-05 cm/cm/°C | |
| MD：-40到40°C | ISO 11359-2 | 7.8E-05 cm/cm/°C | |
| vicat | ASTM D152510 | 125 °C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 116 °C |
| RTI Str | UL 746 | 75.0 °C | |
| vicat | -- | ISO 306/B120 | 130 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 7.6E-05 cm/cm/°C |
| vicat | -- | ISO 306/B50 | 127 °C |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 7.8E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 99.0 °C |
| RTI Imp | UL 746 | 75.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 93.0 °C |
| RTI Elec | UL 746 | 75.0 °C |