PC+ABS PC/ABS M130SHF MARPLEX AUSTRALIA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MARPLEX AUSTRALIA/PC/ABS M130SHF |
|---|---|---|---|
| Impact strength of cantilever beam gap | 3.20mm | ASTM D256 | 500 J/m |
| Dart impact | 3.20mm | ASTM D3029 | 55.0 J |
| hardness | Test Condition | Test Method | MARPLEX AUSTRALIA/PC/ABS M130SHF |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 115 |
| Mechanical properties | Test Condition | Test Method | MARPLEX AUSTRALIA/PC/ABS M130SHF |
|---|---|---|---|
| bending strength | 3.20mm | ASTM D790 | 84.0 MPa |
| elongation | 断裂,3.20mm | ASTM D638 | 120 % |
| tensile strength | 3.20mm | ASTM D638 | 52.0 MPa |
| Flexural modulus | 3.20mm | ASTM D790 | 2400 MPa |
| flammability | Test Condition | Test Method | MARPLEX AUSTRALIA/PC/ABS M130SHF |
|---|---|---|---|
| Hot filament ignition temperature | 1.6mm | AS/NZS60695.2.12 | 550 °C |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | MARPLEX AUSTRALIA/PC/ABS M130SHF |
|---|---|---|---|
| Shrinkage rate | MD：3.00mm | ASTM D955 | 0.60 % |
| Water absorption rate | 24hr | ASTM D570 | 0.25 % |
| melt mass-flow rate | 250°C/3.8kg | ASTM D1238 | 16 g/10min |
| density | ASTM D792 | 1.11 g/cm³ |
| Thermal performance | Test Condition | Test Method | MARPLEX AUSTRALIA/PC/ABS M130SHF |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 99.0 °C |
| vicat | ASTM D15254 | 128 °C | |
| Heat distortion temperature | 1.8MPa,未退火,12.7mm，HDT | ASTM D648 | 105 °C |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 7.2E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 96.0 °C |