Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC XANTAR® MX 1001 Mitsubishi Chemical Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® MX 1001 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/4A | 40 kJ/m² |
| hardness | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® MX 1001 |
|---|---|---|---|
| Rockwell hardness | M计秤 | ISO 2039-2 | 70 |
| Mechanical properties | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® MX 1001 |
|---|---|---|---|
| Nominal tensile fracture strain | ISO 527-2 | >50 % | |
| Tensile modulus | ISO 527-2 | 2200 MPa | |
| Tensile strain | 屈服 | ISO 527-2 | 6.0 % |
| tensile strength | 屈服 | ISO 527-2 | 55.0 MPa |
| Flexural modulus | ISO 178 | 2300 MPa | |
| bending strength | ISO 178 | 80.0 MPa |
| Electrical performance | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® MX 1001 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 29 kV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 2.90 |
| Dissipation Factor | 100Hz | IEC 60250 | 6.6E-04 |
| relative permittivity | 1MHz | IEC 60250 | 2.80 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| Dissipation Factor | 1MHz | IEC 60250 | 9.2E-03 |
| flammability | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® MX 1001 |
|---|---|---|---|
| Burning wire flammability index | 3.00mm | IEC 60695-2-12 | 960 °C |
| Flammability level | 0.750mm | IEC 60695-11-10,-20 | V-0 |
| Limiting Oxygen Index | ISO 4589-2 | 35 % | |
| Flammability level | 1.50mm | IEC 60695-11-10,-20 | V-0 |
| Burning wire flammability index | 1.50mm | IEC 60695-2-12 | 960 °C |
| physical property | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® MX 1001 |
|---|---|---|---|
| Shrinkage rate | MD | ISO 294-4 | 0.60 % |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 21.0 cm³/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.35 % |
| density | ISO 1183 | 1.20 g/cm³ |
| Thermal performance | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® MX 1001 |
|---|---|---|---|
| vicat | ISO 306/B50 | 135 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 115 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6.5E-05 cm/cm/°C |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |