PA66 D.AKV30H2.0 BK LANXESS USA
--
--
Filler: LANXESS, Germany
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LANXESS USA/D.AKV30H2.0 BK |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 55 kJ/m² |
| 23°C | ISO 180/1U | 60 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 75 kJ/m² |
| -30°C | ISO 179/1eU | 60 kJ/m² |
| hardness | Test Condition | Test Method | LANXESS USA/D.AKV30H2.0 BK |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 220 Mpa |
| Supplementary Information | Test Condition | Test Method | LANXESS USA/D.AKV30H2.0 BK |
|---|---|---|---|
| ISO Shortcut | ISO 1874 | PA66.GHR.14-100.GF30 |
| film | Test Condition | Test Method | LANXESS USA/D.AKV30H2.0 BK |
|---|---|---|---|
| Thin film puncture strength | --7 | ISO 6603-2 | 2.80 J |
| --8 | ISO 6603-2 | 2.30 J | |
| --7 | ISO 6603-2 | 900 N | |
| --8 | ISO 6603-2 | 800 N |
| Mechanical properties | Test Condition | Test Method | LANXESS USA/D.AKV30H2.0 BK |
|---|---|---|---|
| bending strength | 3.5%Strain | ISO 178/A | 265 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 3.0 % |
| Flexural modulus | 23°C | ISO 178/A | 9200 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 175 Mpa |
| bending strength | 23°C | ASTM D790 | 270 Mpa |
| FlexuralStrainatFlexuralStrength6(23°C) | 4.0 % | ||
| Tensile modulus | 23°C | ASTM D638 | 9170 Mpa |
| 23°C | ISO 527-2/1 | 10000 Mpa | |
| tensile strength | 断裂,23°C | ASTM D638 | 170 Mpa |
| bending strength | 23°C | ISO 178 | 270 Mpa |
| Nominal tensile fracture strain | 23°C | ISO 527-2/50 | 4.4 % |
| Flexural modulus | 23°C | ASTM D790 | 8690 Mpa |
| elongation | 断裂,23°C | ASTM D638 | 3.0 % |
| Electrical performance | Test Condition | Test Method | LANXESS USA/D.AKV30H2.0 BK |
|---|---|---|---|
| dielectric constant | 23°C,50Hz | IEC 60250 | 4.00 |
| dielectric strength | 23°C,1.00mm | IEC 60243-1 | 35 KV/mm |
| 23°C,3.00mm | IEC 60243-1 | 30 KV/mm | |
| dielectric constant | 23°C,1MHz | IEC 60250 | 4.00 |
| relative permittivity | 23°C,1MHz | IEC 60250 | 4.00 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | V |
| Volume resistivity | 23°C | IEC 60093 | 1E+15 ohms·cm |
| relative permittivity | 23°C,100Hz | IEC 60250 | 4.00 |
| Dissipation Factor | 23°C,50Hz | IEC 60250 | 0.012 |
| Surface Resistivity | IEC 60093 | 1E+15 ohms | |
| Dissipation Factor | 23°C,100Hz | IEC 60250 | 0.012 |
| 23°C,1MHz | IEC 60250 | 0.0190.019 |
| flammability | Test Condition | Test Method | LANXESS USA/D.AKV30H2.0 BK |
|---|---|---|---|
| Burning wire flammability index | 1.6mm | IEC 60695-2-12 | 700 °C |
| 3.0mm | IEC 60695-2-12 | 700 °C | |
| 0.8mm | IEC 60695-2-12 | 700 °C | |
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| Burning Behavior | >1.00mm | ISO 3795 | passed |
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| 3.2mm | UL 94 | HB | |
| 1.5mm | UL 94 | HB | |
| Limiting Oxygen Index | ISO 4589-2 | 23 % | |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | LANXESS USA/D.AKV30H2.0 BK |
|---|---|---|---|
| Shrinkage rate | TD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.13 % |
| Apparent density | ISO 60 | 0.70 g/cm³ | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 2.0 % |
| Shrinkage rate | MD:290°C,2.00mm2 | ISO 294-4 | 0.39 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 5.5 % |
| Shrinkage rate | TD:290°C,2.00mm2 | ISO 294-4 | 0.93 % |
| MD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.070 % |
| Thermal performance | Test Condition | Test Method | LANXESS USA/D.AKV30H2.0 BK |
|---|---|---|---|
| RTI Str | 0.75mm | UL 746 | 110 °C |
| Heat distortion temperature | 0.45MPa,未退火,4.00mm，HDT | ASTM D648 | >249 °C |
| 1.8MPa,未退火,4.00mm，HDT | ASTM D648 | >249 °C | |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 3E-05 cm/cm/°C |
| RTI Imp | 1.5mm | UL 746 | 105 °C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 9E-05 cm/cm/°C |
| ball-indentation hardness | 253°C | IEC 60695-10-2 | Pass |
| RTI Elec | 0.75mm | UL 746 | 125 °C |
| melting temperature | ISO 11357-3 | 263 °C | |
| RTI Imp | 0.75mm | UL 746 | 90.0 °C |
| vicat | -- | ISO 306/B120 | >230 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 250 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | >240 °C | |
| vicat | -- | ISO 306/B50 | 230 °C |
| RTI Str | 1.5mm | UL 746 | 115 °C |
| RTI Elec | 1.5mm | UL 746 | 125 °C |