PC/PTFE DFL22 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electronic and Electrical、Lighting applications
Easy to form、Easy to demould
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/DFL22 |
|---|---|---|---|
| 23°C | ASTMD4812 | 740 J/m | |
| ASTMD256 | 140 J/m | ||
| 23°C3 | ISO180/1U | 49 kJ/m² | |
| 23°C2 | ISO180/1A | 13 kJ/m² | |
| 23°C,EnergyatPeakLoad | ASTMD3763 | 23.2 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/DFL22 |
|---|---|---|---|
| --1 | ASTMD638 | 4140 Mpa | |
| fracture | ASTMD638 | 5.5 % | |
| yield | ASTMD638,ISO527-2 | 3.3 % | |
| 与自身-静态 | ASTMD3702Modified | 0.44 | |
| Bending stress | ISO178 | 118 Mpa | |
| 与自身-动态 | ASTMD3702Modified | 0.38 | |
| Wear factor - Washer | ASTMD3702Modified | 166 10^-10in^5-min/ft-lb-hr | |
| fracture | ASTMD638 | 67.6 Mpa | |
| ISO527-2 | 67.0 Mpa | ||
| yield | ASTMD638 | 71.7 Mpa | |
| ISO527-2 | 71.0 Mpa | ||
| fracture | ISO527-2 | 5.8 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/DFL22 |
|---|---|---|---|
| Vertical flow direction: 24 hours | ISO294-4 | 0.65 % | |
| Flow: 24 hours | ASTMD955 | 0.40到0.60 % | |
| Water absorption rate | 24hr,50%RH | ASTMD570 | 0.10 % |
| Lateral flow: 24 hours | ASTMD955 | 0.60到0.80 % | |
| Flow direction: 24 hours | ISO294-4 | 0.50 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/DFL22 |
|---|---|---|---|
| MD:-40到40°C | ASTME831,ISO11359-2 | 5.6E-05 cm/cm/°C | |
| 0.45MPa, Unanealed, 64.0mm span 4 | ISO75-2/Bf | 146 °C | |
| TD:-40到40°C | ASTME831,ISO11359-2 | 5.6E-05 cm/cm/°C | |
| 0.45MPa, Unanealed, 3.20mm | ASTMD648 | 145 °C | |
| 1.8MPa, Unanealed, 3.20mm | ASTMD648 | 140 °C | |
| 1.8MPa, Unanealed, 64.0mm span 5 | ISO75-2/Af | 140 °C |