Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LCP E6008LMR B SUMITOMO JAPAN
SUMIKASUPER®
Electrical appliances、Automotive sector、Electronic field、Engineering accessories、Food containers、Household appliances、Household appliances、Automotive sector
dimensional stability 、Low warpage、Low viscosity、High rigidity、Good forming performance、Weldable、Aging resistance、Good adhesion、Chemical resistance、heat-resisting、Glass fiber reinforced、high strength
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SUMITOMO JAPAN/E6008LMR B |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 6.40 mm | ASTM D256 | 410 J/m |
| hardness | Test Condition | Test Method | SUMITOMO JAPAN/E6008LMR B |
|---|---|---|---|
| Rockwell hardness | R 级 | ASTM D785 | 103 |
| Mechanical properties | Test Condition | Test Method | SUMITOMO JAPAN/E6008LMR B |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 5.2 % |
| bending strength | 200°C | ASTM D790 | 33.0 Mpa |
| Poisson's ratio | ASTM D785 | 0.46 | |
| Flexural modulus | 200°C | ASTM D790 | 4900 Mpa |
| bending strength | 23°C | ASTM D790 | 143 Mpa |
| shear strength | ASTM D732 | 51.0 Mpa | |
| Flexural modulus | 23°C | ASTM D790 | 12300 Mpa |
| tensile strength | ASTM D638 | 147 Mpa |
| Electrical performance | Test Condition | Test Method | SUMITOMO JAPAN/E6008LMR B |
|---|---|---|---|
| Dissipation Factor | 1 kHz | ASTM D150 | 0.022 |
| Volume resistivity | ASTM D257 | 1.0E+15 ohms·cm | |
| dielectric constant | 1 MHz | ASTM D150 | 3.90 |
| 1 kHz | ASTM D150 | 4.40 | |
| Dissipation Factor | 1 MHz | ASTM D150 | 0.022 |
| arc resistance | ASTM D495 | 130 sec | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| flammability | Test Condition | Test Method | SUMITOMO JAPAN/E6008LMR B |
|---|---|---|---|
| Limiting Oxygen Index | ISO 527-1 | 48 % | |
| Solder resistance | 内部方法 | 300 °C | |
| UL flame retardant rating | 0.30 mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SUMITOMO JAPAN/E6008LMR B |
|---|---|---|---|
| Shrinkage rate | 横向流量 | 内部方法 | 1.2 % |
| Water absorption rate | 饱和 | ASTM D570 | 0.020 % |
| Shrinkage rate | 流量 | 内部方法 | 0.18 % |
| Thermal performance | Test Condition | Test Method | SUMITOMO JAPAN/E6008LMR B |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ASTM D648 | 279 °C |
| Linear coefficient of thermal expansion | 横向 : 150°C | 内部方法 | 5.6E-5 cm/cm/°C |
| thermal conductivity | JIS R2618 | 0.52 W/m/K | |
| Linear coefficient of thermal expansion | 流动 : 150°C | 内部方法 | 1.3E-5 cm/cm/°C |
| injection | Test Condition | Test Method | SUMITOMO JAPAN/E6008LMR B |
|---|---|---|---|
| screw speed | 50 to 100 rpm | ||
| Injection Pressure | 80.0 to 160 Mpa | ||
| Processing (melt) temperature | 360 °C | ||
| drying temperature | 130 °C | ||
| drying time | 4.0 to 24 hr | ||
| pressure holding | 20.0 to 40.0 Mpa | ||
| Temperature in the middle of the barrel | 320 to 350 °C | ||
| Temperature at the rear of the barrel | 280 to 320 °C | ||
| Temperature at the front of the material cylinder | 340 to 370 °C | ||
| Back pressure | 1.00 to 5.00 Mpa | ||
| Temperature | 40 to 160 °C | ||
| injection speed | 中等偏快 | ||
| Spray nozzle temperature | 340 to 370 °C |