Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM UV140LG-BK CELANESE USA
CELCON®
Automotive sector,Automotive interior parts
Low gloss,High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | CELANESE USA/UV140LG-BK |
|---|---|---|---|
| Tensile strain | 屈服 | ISO 527-2/1A/50 | 10 % |
| Tensile modulus | ISO 527-2/1A | 2100 Mpa | |
| tensile strength | 屈服 | ISO 527-2/1A/50 | 48.0 Mpa |
| physical property | Test Condition | Test Method | CELANESE USA/UV140LG-BK |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16 kg | ISO 1133 | 13.0 cm3/10min |
| Shrinkage rate | 流量 | ISO 294-4 | 2.0 % |
| 横向流量 | ISO 294-4 | 1.8 % |
| Thermal performance | Test Condition | Test Method | CELANESE USA/UV140LG-BK |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 168 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 85.0 °C |
| injection | Test Condition | Test Method | CELANESE USA/UV140LG-BK |
|---|---|---|---|
| drying time | 3.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 170 to 180 °C | ||
| Temperature at the rear of the barrel | 170 to 175 °C | ||
| Processing (melt) temperature | 180 to 195 °C | ||
| drying temperature | 100 to 120 °C | ||
| Temperature at the front of the material cylinder | 175 to 185 °C | ||
| Back pressure | < 4.00 Mpa | ||
| Temperature | 80 to 105 °C | ||
| injection speed | 慢 | ||
| Spray nozzle temperature | 185 to 195 °C |