Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC L-1250Z TEIJIN SINGAPORE
PANLITE®
Nursing supplies、Disposable tableware、Medical supplies、Electronic field、Electrical field
High temperature resistan、Low temperature resistanc、heat-resisting、transparent
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TEIJIN SINGAPORE/L-1250Z |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | 76 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179 | 无断裂 |
| Mechanical properties | Test Condition | Test Method | TEIJIN SINGAPORE/L-1250Z |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2400 Mpa | |
| Tensile stress | 屈服 | ISO 527-2/50 | 61.0 Mpa |
| Bending modulus 3 | ISO 178 | 2350 Mpa | |
| Tensile strain | 屈服 | ISO 527-2/50 | 6.0 % |
| Nominal tensile fracture strain | ISO 527-2/50 | > 50 % | |
| Bending stress 3 | ISO 178 | 93.0 Mpa |
| Electrical performance | Test Condition | Test Method | TEIJIN SINGAPORE/L-1250Z |
|---|---|---|---|
| Dissipation Factor | 1 MHz | IEC 60250 | 9.0E-3 |
| CTI | IEC 60112 | 250 V | |
| 100 Hz | IEC 60250 | 3.10 | |
| Volume resistivity | IEC 60093 | > 1.0E+15 ohms·cm | |
| Dissipation Factor | 100 Hz | IEC 60250 | 1.0E-3 |
| Dielectric strength 4 | IEC 60243-1 | 30 KV/mm | |
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms | |
| 1 MHz | IEC 60250 | 3.00 |
| optical performance | Test Condition | Test Method | TEIJIN SINGAPORE/L-1250Z |
|---|---|---|---|
| transmissivity | 3000 µm | ASTM D1003 | 88.0 % |
| refractive index | ASTM D542 | 1.585 |
| flammability | Test Condition | Test Method | TEIJIN SINGAPORE/L-1250Z |
|---|---|---|---|
| Hot filament ignition temperature | 1.5 mm | IEC 60695-2-13 | 850 °C |
| UL flame retardant rating | 0.40 mm | UL 94 | V-2 |
| Hot filament ignition temperature | 3.0 mm | IEC 60695-2-13 | 850 °C |
| Burning wire flammability index | 3.0 mm | IEC 60695-2-12 | 875 °C |
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| Burning wire flammability index | 1.5 mm | IEC 60695-2-12 | 825 °C |
| physical property | Test Condition | Test Method | TEIJIN SINGAPORE/L-1250Z |
|---|---|---|---|
| Shrinkage rate | 横向流量 : 4.00 mm | 内部方法 | 0.50 到 0.70 % |
| 流量 : 4.00 mm | 内部方法 | 0.50 到 0.70 % | |
| density | ISO 1183 | 1.20 g/cm³ | |
| Molten Volume Flow Rate (MVR) | 300°C/1.2 kg | ISO 1133 | 8.00 cm3/10min |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 0.20 % |
| Thermal performance | Test Condition | Test Method | TEIJIN SINGAPORE/L-1250Z |
|---|---|---|---|
| RTI Imp | 0.75 mm | UL 746 | 115 °C |
| 0.45 MPa, 未退火 | ISO 75-2/B | 142 °C | |
| 流动 | ISO 11359-2 | 7.0E-5 cm/cm/°C | |
| 横向 | ISO 11359-2 | 7.0E-5 cm/cm/°C | |
| RTI Elec | 0.75 mm | UL 746 | 125 °C |
| vicat | ISO 306/B50 | 149 °C | |
| RTI | 0.75 mm | UL 746 | 125 °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 129 °C |