LLDPE UF 1810S1 Chandra Asri Petrochemical
--
Bags, linings, films, agricultural applications
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | Chandra Asri Petrochemical/UF 1810S1 |
|---|---|---|---|
| Viscosity | ASTM D3354 | 26.0 g/100cm² |
| film | Test Condition | Test Method | Chandra Asri Petrochemical/UF 1810S1 |
|---|---|---|---|
| elongation | MD:断裂,30µm,吹塑薄膜 | ASTM D882 | 700 % |
| tensile strength | MD:断裂,30µm,吹塑薄膜 | ASTM D882 | 50.0 MPa |
| Elmendorf tear strength | TD:30.0µm | ASTM D1922 | 196.1 kN/m |
| film thickness | 30 µm | ||
| Dart impact | 30µm,吹塑薄膜 | ASTM D1709 | 100 g |
| elongation | TD:断裂,30µm,吹塑薄膜 | ASTM D882 | 850 % |
| tensile strength | TD:断裂,30µm,吹塑薄膜 | ASTM D882 | 24.0 MPa |
| Elmendorf tear strength | MD:30.0µm | ASTM D1922 | 24.5 kN/m |
| Mechanical properties | Test Condition | Test Method | Chandra Asri Petrochemical/UF 1810S1 |
|---|---|---|---|
| coefficient of friction | 铸造薄膜 | ASTM D1894 | 0.060 |
| optical performance | Test Condition | Test Method | Chandra Asri Petrochemical/UF 1810S1 |
|---|---|---|---|
| Haze ratio | 30.0µm,吹塑薄膜 | ASTM D1003 | 20 % |
| transparency | 30.0µm,吹塑薄膜 | ASTM D1746 | 28.0 |
| gloss | 45°,30.0µm,吹塑薄膜 | ASTM D2457 | 46 |
| physical property | Test Condition | Test Method | Chandra Asri Petrochemical/UF 1810S1 |
|---|---|---|---|
| density | ASTM D1505 | 0.922 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 1.0 g/10min |
| Thermal performance | Test Condition | Test Method | Chandra Asri Petrochemical/UF 1810S1 |
|---|---|---|---|
| vicat | ASTM D1525 | 104 °C | |
| brittle temperature | ASTM D746 | <-70.0 °C |