| Impact resistance | Test Condition | Test Method | A SCHULMAN USA/SCHULAKETON NV |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 15 kJ/m² |
| -40°C | ISO 179/1eA | 5.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | A SCHULMAN USA/SCHULAKETON NV |
|---|---|---|---|
| Tensile strain | 屈服 | ISO 527-2/1A/50 | 18 % |
| Tensile modulus | ISO 527-2/1A/1 | 1450 MPa | |
| bending strength | 3.5%应变 | ISO 178 | 40.0 MPa |
| Flexural modulus | ISO 178 | 1500 MPa | |
| tensile strength | 屈服 | ISO 527-2/1A/50 | 65.0 MPa |
| bending strength | 9.0%应变 | ISO 178 | 55.0 MPa |
| flammability | Test Condition | Test Method | A SCHULMAN USA/SCHULAKETON NV |
|---|---|---|---|
| Hot filament ignition temperature | 1.50mm | IEC 60695-2-13 | 725 °C |
| UL flame retardant rating | 1.60mm | UL 94,IEC60695-11-10,-20 | HB |
| Hot filament ignition temperature | 3.00mm | IEC 60695-2-13 | 725 °C |
| burning rate | 2.00mm | ISO 3795 | <100 mm/min |
| UL flame retardant rating | 3.20mm | UL 94,IEC60695-11-10,-20 | HB |
| Burning wire flammability index | 3.00mm | IEC 60695-2-12 | 700 °C |
| 1.50mm | IEC 60695-2-12 | 700 °C |
| physical property | Test Condition | Test Method | A SCHULMAN USA/SCHULAKETON NV |
|---|---|---|---|
| Melt volume flow rate | 240°C/2.16kg | ISO 1133 | 60.0 cm³/10min |
| density | ISO 1183/A | 1.24 g/cm³ |
| Thermal performance | Test Condition | Test Method | A SCHULMAN USA/SCHULAKETON NV |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 100 °C |
| vicat | ISO 306/B50 | 191 °C |