Polyolefin, Unspecified CALP MRP430 Lion Idemitsu Composites Co., Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Lion Idemitsu Composites Co., Ltd./CALP MRP430 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 2.00 kJ/m² |
| hardness | Test Condition | Test Method | Lion Idemitsu Composites Co., Ltd./CALP MRP430 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 112 |
| Mechanical properties | Test Condition | Test Method | Lion Idemitsu Composites Co., Ltd./CALP MRP430 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 2.0 % |
| tensile strength | ASTM D638 | 49.0 MPa | |
| Flexural modulus | ASTM D790 | 6700 MPa | |
| bending strength | ASTM D790 | 75.0 MPa |
| flammability | Test Condition | Test Method | Lion Idemitsu Composites Co., Ltd./CALP MRP430 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Lion Idemitsu Composites Co., Ltd./CALP MRP430 |
|---|---|---|---|
| Shrinkage rate | TD:2.00mm | 内部方法 | 0.70 % |
| density | ASTM D792 | 1.13 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 15 g/10min | |
| Shrinkage rate | MD:2.00mm | 内部方法 | 0.60 % |
| Thermal performance | Test Condition | Test Method | Lion Idemitsu Composites Co., Ltd./CALP MRP430 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 155 °C |