Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 815 SABIC INNOVATIVE US
VALOX™
Automotive External Parts,Electrical applications,medical care
Glass fiber reinforced,High gloss
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/815 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 37 J/m |
| 23°C | ASTM D4812 | 270 J/m |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/815 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 119 |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/815 |
|---|---|---|---|
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 1 |
| Volume resistivity | ASTM D257 | 5.6E+16 ohms·cm | |
| Dissipation Factor | 100Hz | ASTM D150 | 2E-03 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 2 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 2 |
| dielectric constant | 1MHz | ASTM D150 | 3.50 |
| arc resistance | ASTM D495 | PLC 5 | |
| dielectric strength | 3.20mm,inAir | ASTM D149 | 22 KV/mm |
| dielectric constant | 100Hz | ASTM D150 | 3.60 |
| dielectric strength | 1.60mm,在油中 | ASTM D149 | 24 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/815 |
|---|---|---|---|
| tensile strength | Break | ASTM D638 | 89.6 Mpa |
| bending strength | Break,50.0mmSpan | ASTM D790 | 138 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 4480 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/815 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/815 |
|---|---|---|---|
| Shrinkage rate | TD：--3 | 内部方法 | 0.50-0.80 % |
| Water absorption rate | 24hr | ASTM D570 | 0.060 % |
| Shrinkage rate | TD：--4 | 内部方法 | 0.80-1.1 % |
| MD：--2 | 内部方法 | 0.60-0.90 % | |
| density | ASTM D792 | 1.43 g/cm³ | |
| Specific volume | ASTM D792 | 0.704 cm³/g | |
| Shrinkage rate | MD：--3 | 内部方法 | 0.40-0.60 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/815 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 160 °C |
| Linear coefficient of thermal expansion | MD：60to138°C | ASTME831 | 5.4E-05 cm/cm/°C |
| MD：-40to40°C | ASTME831 | 4.5E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 210 °C |
| RTI Imp | UL 746 | 110 °C | |
| RTI Str | UL 746 | 125 °C | |
| RTI Elec | UL 746 | 125 °C |