PPS C-2000SG15 IDEMITSU JAPAN
--
Automotive components
High temperature resistan,Filler: Glass mineral,70% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | IDEMITSU JAPAN/C-2000SG15 |
---|---|---|---|
Impact strength of simply supported beam without notch | ISO 179 | 5.7 kJ/m² |
Supplementary Information | Test Condition | Test Method | IDEMITSU JAPAN/C-2000SG15 |
---|---|---|---|
Flowability2 | 1.00mm,Flowability | 内部方法 | 9.10 CM |
hardness | Test Condition | Test Method | IDEMITSU JAPAN/C-2000SG15 |
---|---|---|---|
Rockwell hardness | M计秤 | ISO 2039-2 | 93 |
Electrical performance | Test Condition | Test Method | IDEMITSU JAPAN/C-2000SG15 |
---|---|---|---|
Dissipation Factor | IEC 60250 | 0.023 | |
dielectric strength | 1.00mm | IEC 60243-1 | 13 KV/mm |
Volume resistivity | ASTM D257 | 1E+16 ohms·cm | |
dielectric constant | IEC 60250 | 6.50 | |
dielectric strength | 3.00mm | IEC 60243-1 | 14 KV/mm |
Mechanical properties | Test Condition | Test Method | IDEMITSU JAPAN/C-2000SG15 |
---|---|---|---|
bending strength | ISO 178 | 161 Mpa | |
Tensile strain | 断裂 | ISO 527-2 | 0.70 % |
Flexural modulus | ISO 178 | 19100 Mpa | |
tensile strength | ISO 527-2 | 89.0 Mpa |
flammability | Test Condition | Test Method | IDEMITSU JAPAN/C-2000SG15 |
---|---|---|---|
UL flame retardant rating | 0.9mm | UL 94 | V-0 |
physical property | Test Condition | Test Method | IDEMITSU JAPAN/C-2000SG15 |
---|---|---|---|
Shrinkage rate | TD | ISO 294-4 | 0.60 % |
MD | ISO 294-4 | 0.35 % | |
Water absorption rate | 23°C,24hr | ISO 62 | 0.010 % |
density | ISO 1183 | 2.10 g/cm³ |
Thermal performance | Test Condition | Test Method | IDEMITSU JAPAN/C-2000SG15 |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 272 °C |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.9E-05 cm/cm/°C |
TD | ISO 11359-2 | 2E-05 cm/cm/°C |